Order Products : sales@su-jiao.com
Diakon® CLH952
| Category: | Acrylic (PMMA) , Polymethyl Methacrylate Acrylic |
| Manufacturer: | Lucite International Inc. |
| Trademark: | Diakon® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | owElv9_Diakon-CLH952.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Diakon®CLH952 is a polymethyl methacrylate-acrylic material,. This product is available in Europe and is processed by extrusion. Diakon®The main features of CLH952 are:
Typical application areas include:
|
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.18 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) | 1.6 | g/10 min | ISO 1133 |
| Water Absorption (Equilibrium, 23°C, 50% RH) | 0.30 | % | ISO 62 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness | 95 | ISO 2039-2 | |
| Ball Indentation Hardness | 185 | MPa | ISO 2039-1 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress (Yield) | 83.0 | MPa | ISO 527-2 |
| Tensile Strain (Yield) | 5.0 | % | ISO 527-2 |
| Flexural Modulus | 3200 | MPa | ISO 178 |
| Flexural Stress | 115 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | 2.0 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength | 20 | kJ/m² | ISO 179/1eU |
| Notched Izod Impact | 1.9 | kJ/m² | ISO 180/1A |
| Instrumented Dart Impact | |||
| -- | 0.400 | J | ASTM D3763 |
| -- | 0.600 | J | ISO 6603-2 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, not annealed | 101 | °C | ISO 75-2/B |
| 1.8 MPa, not annealed | 97.0 | °C | ISO 75-2/A |
| Vicat Softening Temperature | |||
| -- | 110 | °C | ISO 306/A |
| -- | 104 | °C | ISO 306/B |
| CLTE - Flow | 7.1E-5 | cm/cm/°C | ASTM D696 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | HB | UL 94 | |
| Glow Wire Ignition Temperature | 650 | °C | IEC 60695-2-13 |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Refractive Index | 1.490 | ASTM D542, ISO 489 | |
| Transmittance | 92.0 | % | ASTM D1003 |
| Haze | 0.40 | % | ASTM D1003 |
| Additional Information |
|---|
| Mold Shrinkage, H 961/30: .4 to .7%.Craze Resistance (isopropanol), Ineos cantilever test: 2000 secs to break. |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| THERMOLAST® K TC7HAZ (Series: AD/POM) | KRAIBURG TPE | TPE | THERMOLAST® K |
| AURAPENE PPTF20BK | Aurora Manufacturing Ltd | TPO | AURAPENE |
| GAPEX® RPP10EU40BK | Ferro Corporation | PP, Unspecified | GAPEX® |
| Electroblend® PBT-1901 | Colour Image Plastic Compound Sdn. Bhd. (CIPC) | PBT | Electroblend® |
| Karina BLUE PVC COMPOUND 902-06/331-IS (*) | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |