FRAGOM G/458 ES
| Category: | Polyolefin, Unspecified , Polyolefin |
| Manufacturer: | Crosspolimeri S.p.A. |
| Trademark: | FRAGOM |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | ovb2Gv_FRAGOM-G-458-ES.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
FRAGOM : is the trade-mark of our flame retardant halogen free polyolefine compounds. FRAGOM G/458 ES : flame retardant crosslinkable compound suitable for insulation and sheathing of cables of all sections. It is a conveniently grafted compound able to react in presence of moisture and of a catalyst. We normally suggest our catalyst type MAC/100 SCU or MAC/150 SCU (more reactive type). REACTION BETWEEN GRAFTING AND CATALYST These two compounds, separately stored, must be mixed before starting extrusion in the ratio: GRAFTING/CATALYST 95/5 Certify : VDE 0207-24 HM3,BS 7655 EI5 |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.40 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (190°C/21.6 kg) | 7.0 - 12 | g/10 min | ASTM D1238 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore D) | 45 | ASTM D2240 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | > 13.0 | MPa | IEC 60811 |
| Tensile Strain (Break) | > 250 | % | IEC 60811 |
| Aging | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Change in Tensile Strength in Air | IEC 60811 | ||
| 127°C, 40 hr | 15 | % | IEC 60811 |
| 135°C, 168 hr | 20 | % | IEC 60811 |
| Change in Tensile Strain at Break in Air | IEC 60811 | ||
| 127°C, 40 hr | -7.0 | % | IEC 60811 |
| 135°C, 168 hr | -10 | % | IEC 60811 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Thermoset 1 | IEC 60811 | ||
| 200°C | 70 | % | IEC 60811 |
| Residual Value : 200°C | 5.0 | % | IEC 60811 |
| Temperature index- 21% O2 | > 290 | °C | IEC 60811 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Conductivity | µS/mm | IEC 60754-2 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Halogen Content | ppm | IEC 60754-1 | |
| Corrosive gases in flue gas- pH | > 4.30 | IEC 60754-2 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Head Temperature | 205 | °C |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | 4.0E+14 | ohms·cm | IEC 60167 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Oxygen Index | 32 | % | ASTM D2863 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 - 90.0 | °C | |
| Drying Time | 3.0 - 4.0 | hr | |
| Cylinder Zone 1 Temp. | 150 | °C | |
| Cylinder Zone 2 Temp. | 170 | °C | |
| Cylinder Zone 3 Temp. | 180 | °C | |
| Cylinder Zone 4 Temp. | 195 | °C | |
| Die Temperature | 215 | °C |
| Extrusion instructions |
|---|
| CROSSLINKING:Crosslinking of the finished product is obtained by: immersion in hot water at 80/85°C. steam treatment at 0,15 bar. ambient air crosslinking at natural temperature and moisture, after a right number of days depending on climatic conditions. |
| Note Message | |
|---|---|
| 1 . | 20 N/cm2 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Sylvin 86012-66 Clear | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| MOSTEN FC 110 | UNIPETROL RPA | PP Homopolymer | MOSTEN |
| TRIBOCOMP® PPA CF30 TS0 | EPIC Polymers | PPA | TRIBOCOMP® |
| APEX® 155-Y | Teknor Apex Company | PVC, Flexible | APEX® |
| Fiberfil® J-68/30/E | Fiberfil® Engineered Plastics Inc. | PP Copolymer | Fiberfil® |