Borealis PE FA3227
| Category: | LDPE , Low Density Polyethylene |
| Manufacturer: | Borealis AG |
| Trademark: | Borealis PE |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | ovN9wb_Borealis-PE-FA3227.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
FA3227 is a low density polyethylene produced in a high-pressure process. FA3227 is a Low Density Polyethylene for Film Extrusion, UV stabilised. This grade is suitable for building and construction film and meets the requirements for heat, alkali and UV resistance described in the building standards from the Nordic countries. A 150-micron film based upon FA3227 will last at least four times as long as an unstabilised film of the same thickness. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.922 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 0.30 | g/10 min | ISO 1133 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Coefficient of Friction (vs. Itself - Dynamic) | 0.60 | ISO 8295 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film Thickness - Tested | 130 | µm | |
| Film Puncture Energy (130 µm) | 5.00 | J | ASTM D5748 |
| secant modulus | ASTM D882A | ||
| MD : 130 µm | 190 | MPa | ASTM D882A |
| TD : 130 µm | 190 | MPa | ASTM D882A |
| Tensile Strength | ISO 527-3/22 | ||
| MD : 24°C, 130 µm | 25.0 | MPa | ISO 527-3/22 |
| TD : 24°C, 130 µm | 23.0 | MPa | ISO 527-3/22 |
| Tensile Elongation | ISO 527-3 | ||
| MD : Fracture, 130 µm | 400 | % | ISO 527-3 |
| TD : Fracture, 130 µm | 600 | % | ISO 527-3 |
| Dart Drop Impact (130 µm) | 450 | g | ISO 7765-1 |
| Elmendorf Tear Strength | ISO 6383-2 | ||
| MD : 130 µm | 5.0 | N | ISO 6383-2 |
| TD : 130 µm | 6.0 | N | ISO 6383-2 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Melting Temperature | 110 | °C | ISO 11357-3 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Melt Temperature | 170 - 220 | °C |
| Extrusion instructions |
|---|
| Draw down: 70 to 75µm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| DOW™ HDPE NG7005 | The Dow Chemical Company | HDPE | DOW™ HDPE |
| ALTECH® PA66 A 1000/109 | ALBIS PLASTIC GmbH | Nylon 66 | ALTECH® PA66 |
| HiFill® PA4/6 HS LBK | Techmer Engineered Solutions | Nylon 46 | HiFill® |
| K-Bin Rigid PVC KB-6200 | K-Bin, Inc. | PVC, Unspecified | K-Bin Rigid PVC |
| LNP™ LUBRICOMP™ OCL36 compound | SABIC Innovative Plastics | PPS, Linear | LNP™ LUBRICOMP™ |