INNOPOL® PP CS 1-4140 AP
| Category: | PP Homopolymer , Polypropylene Homopolymer |
| Manufacturer: | Inno-Comp Ltd. |
| Trademark: | INNOPOL® PP |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | ovGvy8_INNOPOL-PP-CS-1-4140-AP.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| INNOPOL® CS 1-4140 AP is a 40 % talc-filled, polypropylene homopolymer compound/PP-H TD40 (ISO 1043)/. This grade is available in nature and custom coloured form as well. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Appearance |
|
| Processing Method |
|
| Resin ID (ISO 1043) |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.22 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 5.0 | g/10 min | ISO 1133 |
| Melt Volume-Flow Rate (MVR) (230°C/2.16 kg) | 5.50 | cm³/10min | ISO 1133 |
| Ash Content (600°C) | 39 | % | ISO 3451-1A |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 3500 | MPa | ISO 527-2/1 |
| Tensile Stress (Yield) | 26.0 | MPa | ISO 527-2/50 |
| Tensile Strain (Yield) | 2.5 | % | ISO 527-2/50 |
| Nominal Tensile Strain at Break | 8.0 | % | ISO 527-2 |
| Flexural Modulus 1 | 3700 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | ||
| -30°C | 1.7 | kJ/m² | ISO 179/1eA |
| 23°C | 4.0 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength | ISO 179/1eU | ||
| -30°C | 13 | kJ/m² | ISO 179/1eU |
| 23°C | 30 | kJ/m² | ISO 179/1eU |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, not annealed | 120 | °C | ISO 75-2/B |
| 1.8 MPa, not annealed | 65.0 | °C | ISO 75-2/A |
| Vicat Softening Temperature | |||
| -- | 152 | °C | ISO 306/A120 |
| -- | 78.0 | °C | ISO 306/B120 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating (1.60 mm) | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 | °C | |
| Drying Time | 2.0 | hr | |
| Suggested Max Moisture | 0.070 | % | |
| Rear Temperature | 190 - 250 | °C | |
| Middle Temperature | 190 - 250 | °C | |
| Front Temperature | 190 - 250 | °C | |
| Processing (Melt) Temp | 230 - 260 | °C | |
| Mold Temperature | 10.0 - 50.0 | °C | |
| Injection Rate | Moderate |
| Injection instructions |
|---|
| Hold Pressure: 50 to 100% of injection pressure |
| Note Message | |
|---|---|
| 1 . | 2.0 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 203 GB 10 TFE 13 SI2 | RTP Company | Nylon 66 | RTP |
| ResinDirect COPPI10 | ResinDirect | PP Impact Copolymer | ResinDirect |
| SCANTEC PC M75R | Polykemi AB | PC | SCANTEC |
| YUPLENE® H220P | SK Global Chemical | PP Homopolymer | YUPLENE® |
| Colorite Rigid PVC 2600 NAT | Colorite Polymers | PVC, Rigid | Colorite Rigid PVC |