Durepol® PBT A3 G30 ST MRM0035 BT306
| Category: | PBT , Polybutylene Terephthalate |
| Manufacturer: | Petropol Industry and Trade of Polymers LTDA |
| Trademark: | Durepol® PBT |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | ovDGdq_Durepol-PBT-A3-G30-ST-MRM0035-BT306.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Polyester PBT reinforced with 30% glass fiber, super tough, excellent properties suitable for injection molding. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Processing Method |
|
| Resin ID (ISO 1043) |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.51 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow | 0.30 to 0.90 | % | ASTM D955 |
| Water Absorption (Equilibrium) | 0.15 | % | ASTM D570 |
| Ash Content | 28 to 32 | % | ASTM D2584 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | 115 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 4.1 | % | ASTM D638 |
| Tensile Creep Modulus | ISO 899-1 | ||
| 1 hr | 6200 | MPa | |
| 1000 hr | 4000 | MPa | |
| Flexural Strength | 175 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | 14 | kJ/m² | ASTM D256 |
| Notched Izod Impact (Area) | 12.0 | kJ/m² | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Vicat Softening Temperature | 205 | °C | ASTM D1525 |
| Melting Temperature | 216 | °C | ASTM D2117 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Dissipation Factor | IEC 60250 | ||
| 1.00 mm, 100 Hz | 9.5E-3 | ||
| 1.00 mm, 1 MHz | 0.022 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (1.50 mm) | HB | UL 94 | |
| Glow Wire Ignition Temperature | 750 | °C | IEC 60695-2-13 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 120 | °C | |
| Drying Time | 6.0 | hr | |
| Suggested Max Moisture | 0.020 | % | |
| Processing (Melt) Temp | 240 to 260 | °C | |
| Mold Temperature | 80.0 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| NuSil R2-6755 | NuSil Technology | Silicone | NuSil |
| Cellophane™ 340XSB | Innovia Films Ltd. | Cellulose, Regenerated | Cellophane™ |
| DIC.PPS FZ-3360-M1 | DIC Corporation | PPS | DIC.PPS |
| HI-ZEX™ 5100E | Prime Polymer Co., Ltd. | HDPE | HI-ZEX™ |
| Karina GRAY PVC COMPOUND 950-40/432-IS | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |