VALOX™ ENH4550 resin
| Category: | PBT , Polybutylene Terephthalate |
| Manufacturer: | SABIC Innovative Plastics Europe |
| Trademark: | VALOX™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | oto2io_VALOX-ENH4550-resin.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| 25% GF reinforced, Non-Brominated & Non-Chlorinated Flame Retardant, PBT resin. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| RoHS Compliance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.52 | g/cm³ | ASTM D792, ISO 1183 |
| Melt Mass-Flow Rate (MFR) | ASTM D1238 | ||
| 250°C/5.0 kg | 25 | g/10 min | |
| 265°C/5.0 kg | 25 | g/10 min | |
| Melt Volume-Flow Rate (MVR) | ISO 1133 | ||
| 250°C/5.0 kg | 17.0 | cm³/10min | |
| 265°C/5.0 kg | 17.0 | cm³/10min | |
| Molding Shrinkage | Internal Method | ||
| Flow 1 | 0.10 to 0.50 | % | |
| Flow : 3.20 mm | 0.10 to 0.50 | % | |
| Across Flow 2 | 0.60 to 1.2 | % | |
| Across Flow : 3.20 mm | 0.50 to 1.1 | % | |
| Water Absorption | ISO 62 | ||
| Saturation, 23°C | 0.23 | % | |
| Equilibrium, 23°C, 50% RH | 0.060 | % | |
| UV Weathering - Start F1 from 1mm onword | .75 | UL 746C | |
| Water Immersion - Start F1 from 1mm onword | .75 | UL 746C |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flexural Strain at Break 3 | 2.0 | % | ISO 178 |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Filler Content | 25 | % | ASTM D229 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 124 | ISO 2039-2 | |
| Ball Indentation Hardness (H 358/30) | 174 | MPa | ISO 2039-1 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 4 | 10300 | MPa | ASTM D638 |
| -- | 10400 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Yield 5 | 115 | MPa | ASTM D638 |
| Yield | 112 | MPa | ISO 527-2/5 |
| Break 6 | 115 | MPa | ASTM D638 |
| Break | 112 | MPa | ISO 527-2/5 |
| Tensile Elongation | |||
| Yield 7 | 2.0 | % | ASTM D638 |
| Yield | 2.0 | % | ISO 527-2/5 |
| Break 8 | 2.0 | % | ASTM D638 |
| Break | 2.0 | % | ISO 527-2/5 |
| Flexural Modulus | |||
| 50.0 mm Span 9 | 8500 | MPa | ASTM D790 |
| -- 10 | 9200 | MPa | ISO 178 |
| Flexural Stress | |||
| -- | 175 | MPa | ISO 178 |
| Yield, 50.0 mm Span 11 | 165 | MPa | ASTM D790 |
| Break, 50.0 mm Span 12 | 165 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | |||
| -30°C | 9.0 | kJ/m² | ISO 179/2C |
| 23°C 13 | 5.0 | kJ/m² | ISO 179/1eA |
| 23°C | 9.0 | kJ/m² | ISO 179/2C |
| Charpy Unnotched Impact Strength | ISO 179/2U | ||
| -30°C | 40 | kJ/m² | |
| 23°C | 45 | kJ/m² | |
| Notched Izod Impact | |||
| -30°C | 70 | J/m | ASTM D256 |
| 0°C | 70 | J/m | ASTM D256 |
| 23°C | 70 | J/m | ASTM D256 |
| -30°C 14 | 8.0 | kJ/m² | ISO 180/1A |
| 0°C 15 | 8.0 | kJ/m² | ISO 180/1A |
| 23°C 16 | 8.0 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact | |||
| -30°C | 550 | J/m | ASTM D4812 |
| 23°C | 550 | J/m | ASTM D4812 |
| -30°C 17 | 38 | kJ/m² | ISO 180/1U |
| 23°C 18 | 40 | kJ/m² | ISO 180/1U |
| Instrumented Dart Impact (23°C, Total Energy) | 6.50 | J | ASTM D3763 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, Unannealed, 3.20 mm | 220 | °C | ASTM D648 |
| 0.45 MPa, Unannealed, 64.0 mm Span 19 | 210 | °C | ISO 75-2/Bf |
| 1.8 MPa, Unannealed, 3.20 mm | 205 | °C | ASTM D648 |
| 1.8 MPa, Unannealed, 64.0 mm Span 20 | 220 | °C | ISO 75-2/Af |
| Vicat Softening Temperature | |||
| -- | 215 | °C | ASTM D1525 21 |
| -- | 205 | °C | ASTM D1525, ISO 306/B50 14 22 |
| -- | 220 | °C | ISO 306/A50 |
| -- | 207 | °C | ISO 306/B120 |
| Ball Pressure Test (125°C) | Pass | IEC 60695-10-2 | |
| CLTE | |||
| Flow : -40 to 40°C | 2.3E-5 | cm/cm/°C | ASTM E831 |
| Flow : -40 to 40°C | 2.7E-5 | cm/cm/°C | ISO 11359-2 |
| Flow : 23 to 80°C | 2.2E-5 | cm/cm/°C | ISO 11359-2 |
| Flow : 23 to 150°C | 2.5E-5 | cm/cm/°C | ISO 11359-2 |
| Transverse : -40 to 40°C | 2.3E-5 | cm/cm/°C | ASTM E831 |
| Transverse : -40 to 40°C | 7.1E-5 | cm/cm/°C | ISO 11359-2 |
| Transverse : 23 to 80°C | 9.1E-5 | cm/cm/°C | ISO 11359-2 |
| Transverse : 23 to 150°C | 1.5E-4 | cm/cm/°C | ISO 11359-2 |
| RTI Elec | 130 | °C | UL 746 |
| RTI Imp | 140 | °C | UL 746 |
| RTI Str | 140 | °C | UL 746 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | > 1.0E+15 | ohms | IEC 60093 |
| Volume Resistivity | 1.0E+15 | ohms·cm | ASTM D257, IEC 60093 |
| Dielectric Strength | |||
| 0.800 mm, in Oil | 30 | kV/mm | ASTM D149, IEC 60243-1 |
| 1.60 mm, in Oil | 24 | kV/mm | ASTM D149, IEC 60243-1 |
| 3.20 mm, in Air | 21 | kV/mm | ASTM D149 |
| 3.20 mm, in Oil | 19 | kV/mm | ASTM D149, IEC 60243-1 |
| Dielectric Constant (1 MHz) | 3.40 | ASTM D150, IEC 60250 | |
| Dissipation Factor (1 MHz) | 0.12 | ASTM D150, IEC 60250 | |
| Arc Resistance 23 | PLC 6 | ASTM D495 | |
| Comparative Tracking Index (CTI) | PLC 2 | UL 746 | |
| Comparative Tracking Index | 300 | V | IEC 60112 |
| High Amp Arc Ignition (HAI) | PLC 0 | UL 746 | |
| High Voltage Arc Tracking Rate (HVTR) | PLC 0 | UL 746 | |
| Hot-wire Ignition (HWI) | PLC 0 | UL 746 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 0.300 mm | V-0 | ||
| 2.00 mm | 5VA | ||
| Glow Wire Flammability Index (0.400 mm) | 960 | °C | IEC 60695-2-12 |
| Glow Wire Ignition Temperature | IEC 60695-2-13 | ||
| 0.400 mm | 775 | °C | |
| 0.800 mm | 775 | °C | |
| 3.00 mm | 775 | °C | |
| 3.00 mm 24 | 775 | °C | |
| Oxygen Index | 34 | % | ASTM D2863 |
| Fill Analysis | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Melt Viscosity | ISO 11443 | ||
| 250°C, 1500 sec^-1 | 210 | Pa·s | |
| 260°C, 1500 sec^-1 | 160 | Pa·s |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 110 to 120 | °C | |
| Drying Time | 2.0 to 4.0 | hr | |
| Suggested Max Moisture | 0.020 | % | |
| Hopper Temperature | 40.0 to 60.0 | °C | |
| Rear Temperature | 230 to 240 | °C | |
| Middle Temperature | 235 to 250 | °C | |
| Front Temperature | 240 to 260 | °C | |
| Nozzle Temperature | 230 to 255 | °C | |
| Processing (Melt) Temp | 245 to 260 | °C | |
| Mold Temperature | 40.0 to 100 | °C |
| Note Message | |
|---|---|
| 1 . | Tensile Bar |
| 2 . | Tensile Bar |
| 3 . | 2 mm/min |
| 4 . | 5.0 mm/min |
| 5 . | Type I, 5.0 mm/min |
| 6 . | Type I, 5.0 mm/min |
| 7 . | Type I, 5.0 mm/min |
| 8 . | Type I, 5.0 mm/min |
| 9 . | 1.3 mm/min |
| 10 . | 2.0 mm/min |
| 11 . | 1.3 mm/min |
| 12 . | 1.3 mm/min |
| 13 . | 80*10*4 sp=62mm |
| 14 . | 80*10*4 |
| 15 . | 80*10*4 |
| 16 . | 80*10*4 |
| 17 . | 80*10*4 |
| 18 . | 80*10*4 |
| 19 . | 80*10*4 mm |
| 20 . | 80*10*4 mm |
| 21 . | Rate A (50°C/h), Loading 2 (50 N) |
| 22 . | Rate B (120°C/h), Loading 2 (50 N) |
| 23 . | Tungsten Electrode |
| 24 . | by VDE |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Manner Flexible PVC V903 NAT601 | Manner Plastics, L.P. | PVC, Flexible | Manner Flexible PVC |
| Ravamid® A NC | Ravago Group | Nylon 66 | Ravamid® |
| KEBAFLEX® SG 65 A.01 | BARLOG plastics GmbH | TES | KEBAFLEX® |
| Loyblend® YA-1101 | Colour Image Plastic Compound Sdn. Bhd. (CIPC) | ABS+PBT | Loyblend® |
| Sumikon® FM-TC122 | SBHPP | PC | Sumikon® |