TRIBOCOMP® PA66 TS7
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | EPIC Polymers |
| Trademark: | TRIBOCOMP® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | osDsTk_TRIBOCOMP-PA66-TS7.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| TRIBOCOMP®PA66 TS7 is a polyamide 66 (nylon 66) product,. It is available in Europe. The main characteristics are: lubrication. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Forms |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density | 1.25 | -- | g/cm³ | ISO 1183 |
| Molding Shrinkage - Flow | 1.3 | -- | % | ISO 294-4 |
| Water Absorption (Equilibrium, 23°C, 50% RH) | 2.5 | -- | % | ISO 62 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus (23°C) | 2800 | 1050 | MPa | ISO 527-2 |
| Tensile Stress (Yield, 23°C) | 65.0 | 45.0 | MPa | ISO 527-2 |
| Tensile Strain (Break) | 12 | 20 | % | ISO 527-2 |
| Flexural Modulus (23°C) | 2650 | 900 | MPa | ISO 178 |
| Flexural Stress (23°C) | 80.0 | 55.0 | MPa | ISO 178 |
| Coefficient of Friction | ASTM D3702 | |||
| Dynamic | 0.10 | -- | ASTM D3702 | |
| Static | 0.070 | -- | ASTM D3702 | |
| Wear Factor | 8.00 | -- | ASTM D3702 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 6.0 | -- | kJ/m² | ISO 179 |
| Charpy Unnotched Impact Strength (23°C) | 55 | -- | kJ/m² | ISO 179 |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature | ||||
| 0.45 MPa, not annealed | 220 | -- | °C | ISO 75-2/B |
| 1.8 MPa, not annealed | 80.0 | -- | °C | ISO 75-2/A |
| Electrical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Surface Resistivity | 1.0E+12 | -- | ohms | ASTM D257 |
| Dielectric Strength (2.00 mm) | 30 | -- | kV/mm | IEC 60243-1 |
| Comparative Tracking Index | 600 | -- | V | IEC 60112 |
| Additional Information |
|---|
| 干燥 The value listed as Molding Shrinkage ISO 294-4, was tested in accordance with S.O.P. methods. |
| Injection | Dry | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 | °C | |
| Drying Time | 4.0 | hr | |
| Suggested Max Moisture | 0.10 | % | |
| Rear Temperature | 270 - 300 | °C | |
| Middle Temperature | 275 - 295 | °C | |
| Front Temperature | 270 - 295 | °C | |
| Nozzle Temperature | 280 - 310 | °C | |
| Processing (Melt) Temp | < 300 | °C | |
| Mold Temperature | 80.0 - 100 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Thermec™ 4150R50 | Technical Polymers, LLC | PPS | Thermec™ |
| Chansieh Phenolic J-263-1 | Chansieh Enterprises Co., LTD. | Phenolic | Chansieh Phenolic |
| LNP™ LUBRICOMP™ UCL36ASP compound | SABIC Innovative Plastics Europe | PPA | LNP™ LUBRICOMP™ |
| Plexiglas® Granite | Altuglas International of Arkema Inc. | Acrylic (PMMA) | Plexiglas® |
| POLYfill PPH T3022D | Polykemi AB | PP Homopolymer | POLYfill |