MAJ'ECO EFRHWP304R - 1199
| Category: | PP, Unspecified , Polypropylene |
| Manufacturer: | AD majoris |
| Trademark: | MAJ'ECO |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | os5NXi_MAJ-ECO-EFRHWP304R---1199.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
MAJ'ECO EFRHWP304R-1199 is a flame retardant vegetal fibre polypropylene compound UL 94 V2, in white colour, intended for injection moulding. MAJ'ECO EFRHWP304R-1199 has been developed especially for demanding applications in various engineering sectors. APPLICATIONS Product such as:
|
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.20 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 14 | g/10 min | ISO 1133 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 2520 | MPa | ISO 527-2/1 |
| Tensile Stress (Yield) | 21.0 | MPa | ISO 527-2/50 |
| Flexural Modulus 1 | 2100 | MPa | ISO 178 |
| Flexural Stress 2 | 39.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 6.0 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength (23°C) | 14 | kJ/m² | ISO 179/1eU |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating (1.60 mm) | V-2 | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 90.0 | °C | |
| Drying Time | 4.0 | hr | |
| Processing (Melt) Temp | 140 - 190 | °C | |
| Mold Temperature | 30.0 - 60.0 | °C | |
| Injection Rate | Moderate |
| Injection instructions |
|---|
| Holding pressure: 50 to 70% of the injection pressure |
| Note Message | |
|---|---|
| 1 . | 2.0 mm/min |
| 2 . | at Yield |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Moldex® QS254D/QCM240 | Mitsubishi Chemical Corporation | Polyolefin, Unspecified | Moldex® |
| AIE PA6 50G6 | Asia International Enterprise (Hong Kong) Limited | Nylon 6 | AIE PA6 |
| Alathon® M6080UV | LyondellBasell Industries | HDPE | Alathon® |
| KRALASTIC® ST-600 | Nippon A&L Inc. | ABS | KRALASTIC® |
| LEXAN™ EXL9414T resin | SABIC Innovative Plastics Asia Pacific | PC | LEXAN™ |