SABIC® LLDPE 518N
| Category: | LLDPE , Linear Low Density Polyethylene |
| Manufacturer: | Saudi Basic Industries Corporation (SABIC) |
| Trademark: | SABIC® LLDPE |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | oqLGGL_SABICLLDPE518N.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Product Description 518N is fractional melt index Linear Low Density Polyethylene grade suitable for high strength packaging applications. Films produced using these resins gives outstanding toughness, excellent puncture resistance, good sealing characteristics and machinability on conversion lines. Typical Applications Heavy duty shipping sacks, Ice & frozen food bags, agricultural films etc. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.918 | g/cm³ | ASTM D1505 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 0.50 | g/10 min | ASTM D1238 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film Thickness - Tested | 30 | µm | |
| secant modulus | ASTM D882 | ||
| 1% sectioning, MD : 30 µm | 250 | MPa | ASTM D882 |
| 1% sectioning, TD : 30 µm | 270 | MPa | ASTM D882 |
| Tensile Strength | ASTM D882 | ||
| MD : Yield, 30 µm | 11.0 | MPa | ASTM D882 |
| TD : Yield, 30 µm | 10.0 | MPa | ASTM D882 |
| MD : Break, 30 µm | 45.0 | MPa | ASTM D882 |
| TD : Break, 30 µm | 38.0 | MPa | ASTM D882 |
| Tensile Elongation | ASTM D882 | ||
| MD : Break, 30 µm | 670 | % | ASTM D882 |
| TD : Break, 30 µm | 850 | % | ASTM D882 |
| Dart Drop Impact (30 µm) | 140 | g | ASTM D1709 |
| Elmendorf Tear Strength | ASTM D1922 | ||
| MD : 30 µm | 180 | g | ASTM D1922 |
| TD : 30 µm | 400 | g | ASTM D1922 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Vicat Softening Temperature | 102 | °C | ASTM D1525 |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Gloss (45°, 30.0 µm) | 80 | ASTM D2457 | |
| Haze (30.0 µm) | 12 | % | ASTM D1003 |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Puncture Resistance (30.0 µm) | 890 | J/cm | Internal method |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Melt Temperature | 205 - 220 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| TAROPRENE® 1 A40 M1N | Taro Plast S.p.A. | TPV | TAROPRENE® |
| BP Flex 7000 VPL BLK | Buckeye Polymers, Inc. | TPV | BP Flex |
| Daelim Po1y® PP-101S | DAELIM INDUSTRIAL CO., LTD. | PP, Unspecified | Daelim Po1y® |
| Kingfa PP-V15 | Kingfa | PP, Unspecified | Kingfa |
| Durethan® BKV 40 H3.0 000000 | LANXESS Corporation | Nylon 6 | Durethan® |