Greenflex® ML 50 F
| Category: | EVA , Ethylene Vinyl Acetate Copolymer |
| Manufacturer: | Versalis S.p.A. |
| Trademark: | Greenflex® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | oqAbh6_Greenflex-ML-50-F.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Greenflex ML 50 F is an ethylene vinyl acetate copolymer (EVA) for injection moulding, compounding and extrusion. Main Application Greenflex ML 50 F is recommended for the production of foamed and crosslinked sheets for shoes, dolls, shock absorbers and gasket. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.941 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 2.5 | g/10 min | ISO 1133 |
| Vinyl Acetate Content | 19.0 | wt% | Internal Method |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Shore Hardness | ISO 868 | ||
| Shore A, Injection Molded | 89 | ||
| Shore D, Injection Molded | 36 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress (Yield, Injection Molded) | 4.50 | MPa | ISO 527-2 |
| Flexural Modulus (Injection Molded) | 40.0 | MPa | ISO 178 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Brittleness Temperature | < -80.0 | °C | ASTM D746 |
| Vicat Softening Temperature | 58.0 | °C | ISO 306/A |
| Melting Temperature | 83.0 | °C | Internal Method |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Processing (Melt) Temp | 140 to 200 | °C | |
| Mold Temperature | 10.0 to 30.0 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Miramid® VX30CF | BASF Leuna GmbH | Nylon 6 | Miramid® |
| Nypol® PA A3 G30 HS UV RH AMLA144 NR450 MSP | Petropol Industry and Trade of Polymers LTDA | Nylon 66 | Nypol® PA |
| DINAPLEN® PPH1S05 M403 H-4166 | Grupo Repol | PP Homopolymer | DINAPLEN® |
| LEXAN™ ML7667 resin | SABIC Innovative Plastics | PC | LEXAN™ |
| Innoprene 1450N/B | Kumho Polychem Co., Ltd. | TPV | Innoprene |