PETLIN LD C150Y
| Category: | LDPE , Low Density Polyethylene |
| Manufacturer: | PETLIN (MALAYSIA) SDN BHD |
| Trademark: | PETLIN |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | oq0V4Z_PETLIN-LD-C150Y.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| PETLIN LD C150Y is a low density polyethylene resin for general purpose and film applications. It is produced by the state-of-the-art DSM Stamicarbon tubular process. It contains antioxidant (BHT free), slip and antiblock additives. It is intended primarily for blown film process. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.921 | g/cm³ | ISO 1183/A |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 5.0 | g/10 min | ISO 1133 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Coefficient of Friction | 0.10 | ASTM D1894 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film Thickness - Tested | 25 | µm | |
| Film Thickness - Recommended / Available | 150 to 60 µm | ||
| Tensile Modulus | ISO 527-3 | ||
| MD : 25 µm | 202 | MPa | |
| TD : 25 µm | 224 | MPa | |
| Tensile Stress | ISO 527-3 | ||
| MD : Break, 25 µm | 26.0 | MPa | |
| TD : Break, 25 µm | 15.0 | MPa | |
| Tensile Elongation | ISO 527-3 | ||
| MD : Break, 25 µm | 150 | % | |
| TD : Break, 25 µm | 610 | % | |
| Dart Drop Impact (25 µm) | 86 | g | ASTM D1709 |
| Elmendorf Tear Strength | ISO 6383-2 | ||
| MD : 25 µm | 80000 | N | |
| TD : 25 µm | 30000 | N |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Gloss (45°, 25.0 µm) | 66 | ASTM D2457 | |
| Haze (25.0 µm) | 6.5 | % | ASTM D1003 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Melt Temperature | 145 to 165 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Tenac™ LT805 | Asahi Kasei Chemicals Corporation | Acetal (POM) Homopolymer | Tenac™ |
| TOPAS® 8007D-61 | Topas Advanced Polymers, Inc. | COC | TOPAS® |
| Niretan A F35 | Soredi S.p.a. | Nylon 66 | Niretan A |
| Alathon® M6080 | LyondellBasell Industries | HDPE | Alathon® |
| HiFill® HDPE GF30 CC | Techmer Engineered Solutions | HDPE | HiFill® |