RC Plastics RCPA66 GF 30
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | RC Plastics, Inc. (Div. of LNP Engineering Plastics) |
| Trademark: | RC Plastics |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | opd7Ou_RC-Plastics-RCPA66-GF-30.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| RC Plastics RCPA66 GF 30 is a Polyamide 66 (Nylon 66) product filled with 30% glass fiber. It can be processed by injection molding and is available in North America. Primary characteristic: eco-friendly/green. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Recycled Content |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.37 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow (3.18 mm) | 0.40 to 0.55 | % | ASTM D955 |
| Water Absorption (Equilibrium, 23°C, 50% RH) | 0.90 | % | ASTM D570 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | 168 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 3.5 | % | ASTM D638 |
| Flexural Modulus | 8070 | MPa | ASTM D790 |
| Flexural Strength | 247 | MPa | ASTM D790 |
| Coefficient of Friction | ASTM D1894 | ||
| vs. Itself - Dynamic | 0.31 | ||
| vs. Itself - Static | 0.25 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (3.18 mm) | 93 | J/m | ASTM D256 |
| Unnotched Izod Impact | 850 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 249 | °C | ASTM D648 |
| Melting Temperature | 260 | °C |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 82.2 | °C | |
| Drying Time | 4.0 to 6.0 | hr | |
| Rear Temperature | 277 to 304 | °C | |
| Middle Temperature | 277 to 304 | °C | |
| Front Temperature | 277 to 304 | °C | |
| Processing (Melt) Temp | 282 to 302 | °C | |
| Mold Temperature | 65.6 to 107 | °C | |
| Injection Rate | Fast | ||
| Back Pressure | 0.345 to 0.689 | MPa | |
| Screw Speed | 30 to 100 | rpm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SLOVAMID® 6 LI | Plastcom | Nylon 6 | SLOVAMID® 6 |
| TEREZ PA 6 7500 GF25 | TER HELL PLASTIC GMBH | Nylon 6 | TEREZ PA 6 |
| 3M™ Dyneon™ TFM™ Modified PTFE Compound TFM 4213 | 3M Advanced Materials Division | PTFE | 3M™ Dyneon™ TFM™ Modified PTFE Compound |
| ALTECH® PP-H B 4930/506 MR30 | ALBIS PLASTIC GmbH | PP Homopolymer | ALTECH® PP-H |
| PENTAMID B L5 H natur | PENTAC Polymer GmbH | Nylon 6 | PENTAMID B |