Diakon® CLG340
| Category: | Acrylic (PMMA) , Polymethyl Methacrylate Acrylic |
| Manufacturer: | Lucite International Inc. |
| Trademark: | Diakon® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | op5W2A_Diakon-CLG340.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Diakon®CLG340 is a polymethyl methacrylate-acrylic material,. This product is available in Europe and is processed by extrusion or injection molding. Diakon®The main characteristics of CLG340 are: flame retardant/rated flame. |
| General Information | |
|---|---|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.18 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) | 19 | g/10 min | ISO 1133 |
| Water Absorption (Equilibrium, 23°C, 50% RH) | 0.30 | % | ISO 62 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (M-Scale) | 80 | ISO 2039-2 | |
| Ball Indentation Hardness | 170 | MPa | ISO 2039-1 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress (Yield) | 70.0 | MPa | ISO 527-2 |
| Tensile Strain (Yield) | 3.5 | % | ISO 527-2 |
| Flexural Modulus | 2900 | MPa | ISO 178 |
| Flexural Stress | 95.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | 1.8 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength | 18 | kJ/m² | ISO 179/1eU |
| Notched Izod Impact | 1.8 | kJ/m² | ISO 180/1A |
| Multi-Axial Instrumented Impact Energy | 0.300 | J | ISO 6603-2 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, not annealed | 88.0 | °C | ISO 75-2/B |
| 1.8 MPa, not annealed | 85.0 | °C | ISO 75-2/A |
| Vicat Softening Temperature | |||
| -- | 95.0 | °C | ISO 306/A |
| -- | 90.0 | °C | ISO 306/B |
| CLTE - Flow | 7.1E-5 | cm/cm/°C | ASTM D696 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | HB | UL 94 | |
| Glow Wire Ignition Temperature | 650 | °C | IEC 60695-2-13 |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Refractive Index | 1.490 | ISO 489 | |
| Transmittance | 92.0 | % | ASTM D1003 |
| Haze | 0.40 | % | ASTM D1003 |
| Additional Information |
|---|
| Mold Shrinkage, H 961/30: .4 to .7 %.Craze Resistance (isopropanol), Ineos cantilever test: 30 secs to break. |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Manner Flexible PVC X3364 | Manner Plastics, L.P. | PVC, Flexible | Manner Flexible PVC |
| Caltex PP MR43SM | GS Caltex | PP, Unspecified | Caltex PP |
| Evermore PUR UP-9120NHR | Evermore Chemical Industry Co., Ltd. | PUR-PC | Evermore PUR |
| Iupilon® DH3002R | Mitsubishi Engineering-Plastics Corp | PC | Iupilon® |
| Sylvin 8498-72 Natural | Sylvin Technologies Incorporated | PVC+NBR | Sylvin |