Ensinger HYDLAR® Z
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | Ensinger Inc. |
| Trademark: | Ensinger |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | oohYGb_Ensinger-HYDLAR-Z.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
HYDLAR™ possesses a combination of physical properties that cannot be found in any other commercially available engineered plastic. Design engineers have created a family of superior wear and abrasion resistant thermoplastics using aramid fiber reinforcement. HYDLAR® is applicable to a wide variety of industrial applications where high strength, extreme wear resistance and low abrasiveness are required.Typical applications would be wear strips, bearings, bushings, rollers, gears and wherever wear and abrasion resistant materials are required. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.16 | g/cm³ | ASTM D792 |
| Water Absorption | ASTM D570 | ||
| 24 hr | 0.80 | % | ASTM D570 |
| Saturated, 23°C | 6.3 | % | ASTM D570 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 8960 | MPa | ASTM D638 |
| Tensile Strength (Break) | 110 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 4.0 | % | ASTM D638 |
| Flexural Modulus | 6210 | MPa | ASTM D790 |
| Flexural Strength | 159 | MPa | ASTM D790 |
| Compressive Strength | 133 | MPa | ASTM D695 |
| Wear Factor 1(1.7 MPa, 0.051 m/sec) | 160 - 260 | 10^-8 mm³/N·m | ASTM D3702 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | 140 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 243 | °C | ASTM D648 |
| Continuous Use Temperature | 149 | °C | |
| CLTE - Flow | 2.9E-5 | cm/cm/°C | ASTM D696 |
| Additional Information |
|---|
| Data obtained from extruded shapes material. |
| Note Message | |
|---|---|
| 1 . | PV=2500 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| MARPOL® EVA 28800 | Marco Polo International, Inc. | EVA | MARPOL® EVA |
| Nanjing Hongrui PA66 A1000 | Nanjing Hongrui Engineering Plastics Co., Ltd. | Nylon 66 | Nanjing Hongrui PA66 |
| Hifax TYC 356P | LyondellBasell Industries | Polyolefin, Unspecified | Hifax |
| Karina WHITE PVC COMPOUND -E818-10/23-CRM | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| SQUARE® LIM3630-30A/B | Shenzhen SQUARE Silicone Co., Ltd. | Silicone Rubber, LSR | SQUARE® |