Latamid 66 H2 K/50
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | LATI S.p.A. |
| Trademark: | Latamid |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | onso4i_Latamid-66-H2-K-50.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Compound based on Polyamide 66 (PA 66). Heat stabilised. Carbon fibre. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.37 | g/cm³ | ISO 1183 |
| Molding Shrinkage 1 | ISO 294-4 | ||
| Across Flow : 2.00 mm | 0.35 to 0.55 | % | |
| Flow : 2.00 mm | 0.10 to 0.30 | % |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | ISO 527-2/1 | ||
| 23°C | 29000 | MPa | |
| 60°C | 27000 | MPa | |
| 90°C | 17500 | MPa | |
| 120°C | 12000 | MPa | |
| 150°C | 9500 | MPa | |
| Tensile Stress | ISO 527-2/5 | ||
| Break, 23°C | 210 | MPa | |
| Break, 60°C | 170 | MPa | |
| Break, 90°C | 140 | MPa | |
| Break, 120°C | 125 | MPa | |
| Break, 150°C | 100 | MPa | |
| Tensile Strain | ISO 527-2/5 | ||
| Break, 23°C | 1.0 | % | |
| Break, 60°C | 1.5 | % | |
| Break, 90°C | 2.4 | % | |
| Break, 120°C | 2.8 | % | |
| Break, 150°C | 2.9 | % |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 7.0 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength (23°C) | 35 | kJ/m² | ISO 179/1eU |
| Notched Izod Impact (23°C, 3.20 mm) | 70 | J/m | ASTM D256A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, Unannealed | 260 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 255 | °C | ISO 75-2/A |
| Continuous Use Temperature 2 | 135 | °C | |
| Vicat Softening Temperature | 255 | °C | ISO 306/B50 |
| CLTE - Flow (30 to 100°C) | 2.0E-6 | cm/cm/°C | ASTM D696 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 10 | ohms | ASTM D257 |
| Volume Resistivity | 50 | ohms·cm | ASTM D257 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 90.0 to 100 | °C | |
| Drying Time | 3.0 | hr | |
| Processing (Melt) Temp | 280 to 310 | °C | |
| Mold Temperature | 80.0 to 100 | °C | |
| Injection Rate | Moderate |
| Note Message | |
|---|---|
| 1 . | at 60 Mpa of cavity pressure |
| 2 . | 20,000 hr |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Purgex™ 3057 Plus | Neutrex, Inc. | PE, Unspecified | Purgex™ |
| NEXT REGRIND POMC M90-300RG | NEXT Specialty Resins, Inc. | Acetal (POM) Copolymer | NEXT REGRIND |
| Baynat® 755 Isocyanate | Covestro - PUR | PUR, Unspecified | Baynat® |
| ISOPAK® 547 | Great Eastern Resins Industrial Co Ltd (GRECO) | ABS | ISOPAK® |
| Pier One PC/PBT 1102 | Pier One Polymers, Inc. | PC+PBT | Pier One PC/PBT |