Ultrathene® UE637000
| Category: | EVA , Ethylene Vinyl Acetate Copolymer |
| Manufacturer: | LyondellBasell Industries |
| Trademark: | Ultrathene® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | omTquF_Ultrathene-UE637000.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| ULTRATHENE UE 637-000 is an EVA copolymer with good toughness, flexibility and clarity. Applications include laminating and heavy duty films as well as injection and blow molding. UE 637-000 contains no additives. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 3.2 | g/10 min | ASTM D1238 |
| Vinyl Acetate Content | 9.0 | wt% |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness | ASTM D2240 | ||
| Shaw A | 94 | ASTM D2240 | |
| Shaw D | 33 | ASTM D2240 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 1(Break) | 13.8 | MPa | ASTM D638 |
| Tensile Elongation 2(Break) | 700 | % | ASTM D638 |
| Flexural Modulus | 79.3 | MPa | ASTM D790 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| secant modulus | ASTM D882 | ||
| 1% secant, MD | 84.8 | MPa | ASTM D882 |
| 1% secant, TD | 91.0 | MPa | ASTM D882 |
| Tensile Strength | ASTM D882 | ||
| MD : Yield | 6.23 | MPa | ASTM D882 |
| TD : Yield | 5.81 | MPa | ASTM D882 |
| MD : Fracture | 25.9 | MPa | ASTM D882 |
| TD : Fracture | 18.9 | MPa | ASTM D882 |
| Tensile Elongation | ASTM D882 | ||
| MD : Fracture | 350 | % | ASTM D882 |
| TD : Fracture | 500 | % | ASTM D882 |
| Dart Drop Impact (51 µm) | 400 | g | ASTM D1709 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Brittleness Temperature | -76.0 | °C | ASTM D746 |
| Vicat Softening Temperature | 80.0 | °C | ASTM D1525 |
| Additional Information |
|---|
| Elongation at Break, ASTM D638, Type IV, 20 in/min: >700% |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Melt Temperature | 221 | °C |
| Extrusion instructions |
|---|
| Maximum recommended melt temperature: 430°F (221°C). |
| Note Message | |
|---|---|
| 1 . | Type 4, 510mm/min |
| 2 . | Type 4, 510mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| WELLAMID Nylon 6000 HWCP | CP-Polymer-Technik GmbH & Co. KG | Nylon 6 | WELLAMID Nylon |
| NEFTEKHIM ABS 0445E | Nizhnekamskneftekhim Inc. | ABS | NEFTEKHIM ABS |
| Novalloy-B B6526 | PlastxWorld Inc. | ABS+PBT | Novalloy-B |
| Devcon Plastic Steel® Liquid (B) | Devcon | Epoxy | Devcon |
| LNP™ STAT-KON™ RD000 compound | SABIC Innovative Plastics | Nylon 66 | LNP™ STAT-KON™ |