Generic Epoxy - Mineral
| Category: | Epoxy , Epoxy; Epoxide |
| Manufacturer: | Generic |
| Trademark: | Generic |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | omN76t_Generic-Epoxy---Mineral.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
This data represents typical values that have been calculated from all products classified as: Generic Epoxy - Mineral This information is provided for comparative purposes only. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.59 to 2.07 | g/cm³ | ASTM D792 |
| Apparent Density | 0.80 to 0.91 | g/cm³ | ASTM D1895 |
| Molding Shrinkage - Flow (23°C) | 0.24 to 0.60 | % | ASTM D955 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Break, 23°C) | 34.5 to 90.0 | MPa | ASTM D638 |
| Flexural Modulus (23°C) | 13600 to 20000 | MPa | ASTM D790 |
| Flexural Strength (Break, 23°C) | 119 to 150 | MPa | ASTM D790 |
| Compressive Strength (23°C) | 110 to 272 | MPa | ASTM D695 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 19 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 1.8 MPa, Unannealed | 225 to 236 | °C | |
| 1.8 MPa, Annealed | 275 to 282 | °C | |
| CLTE - Flow | |||
| -- | 1.8E-5 to 4.0E-5 | cm/cm/°C | ASTM D696 |
| -- | 2.2E-5 to 2.4E-5 | cm/cm/°C | ASTM E831 |
| Thermal Conductivity (23°C) | 0.70 to 0.72 | W/m/K | ASTM C177 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Dielectric Strength (23°C) | 13 to 18 | kV/mm | ASTM D149 |
| Dielectric Constant (23°C) | 3.74 to 5.31 | ASTM D150 | |
| Dissipation Factor (23°C) | 6.0E-3 to 0.020 | ASTM D150 | |
| Arc Resistance | 180 to 181 | sec | ASTM D495 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 6042-70A MD | RTP Company | TPE | RTP |
| Tenac™ 5013A | Asahi Kasei Chemicals Corporation | Acetal (POM) Homopolymer | Tenac™ |
| Wanthane® WHT-1180 | Wanhua Chemical Group Co., Ltd. | TPU-Polyester | Wanthane® |
| Flexoprene® 95 | Puma Tecnica S.A.I.C.F.I | PE, Unspecified | Flexoprene® |
| Rotuba CAB B9086 (10% Plasticizer) | Rotuba Extruders, Inc. | CAB | Rotuba CAB |