Boda BDPL-H2701

Category:	Fluorelastomer , Fluoroelastomer
Manufacturer:	Chenguang Fluoro & Silicone Elastomers Co., Ltd.
Trademark:	Boda
Fillers:	-
Ports:	Qinzhou, Shekou, Shanghai, Ningbo
Delivery Terms	FOB, CIF, DAP, DAT, DDP
PDF:	ok5Lgd_Boda-BDPL-H2701.pdf
PRICE:	Order Products email sales@su-jiao.com

Wechat: WECHAT

WECHAT

Message

Material Type: Black color low-temp grade fluoroelastomer compound, hardness
Shore A 65~75.Based on peroxide curable fluoroelastomer with high fluorine content.

Features:

Short post cure time

Excellent mold flow and mold release, resulting in less flash

Low temperature grade, tr10 -24°C

Extraordinary chemical resistance:

Alcohol Fuel

Steam

Acids

Chemicals containing amines.

Process Methods: Suitable for compression, transfer molding processes.

Applications: Fuel injector O-ring and other low temperature sealing parts.

Lab Testing Curing Condition:

Press Curing: 10min@170°C.

Oven: (1+4)hrs@230°C

General Information
Features	Acid Resistant Alcohol Resistant Fuel Resistant Good Chemical Resistance Good Flow Good Mold Release Good Moldability Low Temperature Resistant Minimal Flash Steam Resistant
Uses	Seals
Appearance	Black
Processing Method	Compression Molding Resin Transfer Molding

Physical	Nominal Value	Unit	Test Method
Specific Gravity	1.98	g/cm³	ASTM D792

Hardness	Nominal Value	Unit	Test Method
Durometer Hardness (Shore A)	72		ASTM D2240

Elastomers	Nominal Value	Unit	Test Method
Tensile Strength (Yield)	18.0	MPa	ASTM D412
Tensile Elongation (Break)	190	%	ASTM D412
Compression Set ¹(200°C, 70 hr)	20	%	ASTM D395

Aging	Nominal Value	Unit	Test Method
Change in Tensile Strength in Air (250°C, 70 hr)	-12	%	ASTM D573
Change in Ultimate Elongation in Air (250°C, 70 hr)	-7.0	%	ASTM D573
Change in Durometer Hardness in Air (250°C, 70 hr)	2.0		ASTM D573
Change in Tensile Strength (23°C, 70 hr, in Reference Fuel C)	-9.0	%	ASTM D471
Change in Ultimate Elongation (23°C, 70 hr, in Reference Fuel C)	-5.0	%	ASTM D471
Change in Durometer Hardness (23°C, 70 hr, in Reference Fuel C)	-2.0		ASTM D471
Change in Volume (23°C, 70 hr, in Reference Fuel C)	3.0	%	ASTM D471

Note Message
1 .	6 mm Buttons

Resin Grade	Manufacturer	Category	Trademark
Mirakutoran® TPU E380PKOO	Japan Mirakutoran Inc.	TPU Alloy	Mirakutoran® TPU
3M™ Dyneon™ TFM™ Modified PTFE Compound TFM 6302	3M Advanced Materials Division	PTFE	3M™ Dyneon™ TFM™ Modified PTFE Compound
Braskem PE LL6901S	Braskem	LLDPE	Braskem PE
Dryflex® 4057	ELASTO	TPE	Dryflex®
Hostacom CR 250 F C11274	LyondellBasell Industries	PP, Unspecified	Hostacom