PRL PC-HM-FR1-(color)-1
| Category: | PC , Polycarbonate |
| Manufacturer: | Polymer Resources Ltd. |
| Trademark: | PRL |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | oitnPi_PRL-PC-HM-FR1--color--1.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
PRL PC-HM-FR1-(color)-1 is a Polycarbonate (PC) product filled with 10% glass fiber. It can be processed by injection molding and is available in North America. Characteristics include:
|
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| RoHS Compliance |
|
| UL File Number |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.26 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (300°C/1.2 kg) | 5.0 to 12 | g/10 min | ASTM D1238 |
| Molding Shrinkage | ASTM D955 | ||
| Flow : 3.18 mm | 0.20 to 0.50 | % | |
| Across Flow : 3.18 mm | 0.20 to 0.50 | % |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness | ASTM D785 | ||
| M-Scale | 85 | ||
| R-Scale | 124 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | ASTM D638 | ||
| Yield, 3.18 mm | 65.5 | MPa | |
| Break, 3.18 mm | 55.8 | MPa | |
| Tensile Elongation | ASTM D638 | ||
| Yield, 3.18 mm | 6.0 | % | |
| Break, 3.18 mm | 15 | % | |
| Flexural Modulus (3.18 mm) | 3380 | MPa | ASTM D790 |
| Flexural Strength (3.18 mm) | 103 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C, 3.18 mm) | 110 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, Unannealed, 3.18 mm | 143 | °C | |
| 1.8 MPa, Unannealed, 3.18 mm | 138 | °C | |
| Vicat Softening Temperature | 152 | °C | ASTM D1525 1 |
| RTI Elec | UL 746 | ||
| 1.50 mm | 80.0 | °C | |
| 3.00 mm | 80.0 | °C | |
| RTI Imp | UL 746 | ||
| 1.50 mm | 80.0 | °C | |
| 3.00 mm | 80.0 | °C | |
| RTI Str | UL 746 | ||
| 1.50 mm | 80.0 | °C | |
| 3.00 mm | 80.0 | °C |
| Electrical | Nominal Value | Test Method | |
|---|---|---|---|
| Comparative Tracking Index (CTI) (1.50 mm) | PLC 3 | UL 746 | |
| High Amp Arc Ignition (HAI) | UL 746 | ||
| 1.50 mm | PLC 1 | ||
| 3.00 mm | PLC 1 | ||
| Hot-wire Ignition (HWI) | UL 746 | ||
| 1.50 mm | PLC 2 | ||
| 3.00 mm | PLC 1 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 1.50 mm, ALL | V-0 | ||
| 3.00 mm, ALL | V-0 5VA |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 118 to 124 | °C | |
| Drying Time | 3.0 to 4.0 | hr | |
| Drying Time, Maximum | 8.0 | hr | |
| Rear Temperature | 293 to 316 | °C | |
| Middle Temperature | 304 to 327 | °C | |
| Front Temperature | 316 to 338 | °C | |
| Processing (Melt) Temp | 302 to 329 | °C | |
| Mold Temperature | 82.2 to 116 | °C |
| Note Message | |
|---|---|
| 1 . | Rate B (120°C/h), Loading 2 (50 N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 207 HB | RTP Company | Nylon 66 | RTP |
| WanBlend® WHT-1175M | Wanhua Chemical Group Co., Ltd. | TPU-Polyester | WanBlend® |
| Bormed™ RD808CF | Borealis AG | PP Random Copolymer | Bormed™ |
| DOMAMID® A1-002-V15-N | DOMO Engineering Plastics GmbH | Nylon 6 | DOMAMID® |
| Lucky Enpla LPC1000 | Lucky Enpla Co LTD | PC | Lucky Enpla |