Braskem PE LH-118
| Category: | LLDPE , Linear Low Density Polyethylene |
| Manufacturer: | Braskem |
| Trademark: | Braskem PE |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | ogGYVP_Braskem-PE-LH-118.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Description: LH118 is a Linear Low Density Polyethylene, copolymer of hexene-1, produced by Spherilene process. Developed for blown film extrusion in blends with polyethylenes. Films obtained with this product show a good processing performance balanced with good optical and mechanical properties as well as sealability. Very low gel amount. It contains antioxidant additives. Applications: Stretch films; liners; LDPE and HDPE blends and packages for general use. Others applications: blends for irrigation pipes. Process: Recommended processing conditions for film extrusion about 170 - 210 °C. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.916 | g/cm³ | ASTM D1505 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 1.0 | g/10 min | ASTM D1238 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film Thickness - Tested | 38 | µm | |
| Tensile Strength | ASTM D882 | ||
| MD : Fracture | 40.0 | MPa | ASTM D882 |
| TD : Fracture | 40.0 | MPa | ASTM D882 |
| Tensile Elongation | ASTM D882 | ||
| MD : Fracture | 1100 | % | ASTM D882 |
| TD : Fracture | 1400 | % | ASTM D882 |
| Flexural Modulus | ASTM D790 | ||
| 1% Secant, MD | 200 | MPa | ASTM D790 |
| 1% Secant, TD | 210 | MPa | ASTM D790 |
| Dart Drop Impact | 150 | g | ASTM D1709 |
| Elmendorf Tear Strength | ASTM D1922 | ||
| MD | 300 | g | ASTM D1922 |
| TD | 510 | g | ASTM D1922 |
| Optical | Nominal Value | Test Method | |
|---|---|---|---|
| Gloss (60°) | 69 | ASTM D2457 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Melt Temperature | 170 - 210 | °C |
| Extrusion instructions |
|---|
| Blow up Ratio: 2.2:1 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SABIC® PP CPC35C | Saudi Basic Industries Corporation (SABIC) | PP Copolymer | SABIC® PP |
| Siloxane Masterbatch MB50-320 | Multibase, A Dow Corning Company | Siloxane, UHMW | Siloxane Masterbatch |
| Zhongfa PC FR2840G | Yuyao Zhongfa Engineering Plastics Co. Ltd. | PC | Zhongfa |
| Expandable PS F11B | INEOS Styrenics International SA | PS (EPS) | Expandable PS |
| LUVOCOM® 1-1119-1 VP | Lehmann & Voss & Co. | Nylon 66 | LUVOCOM® |