NEXUS PC PC1212R
| Category: | PC , Polycarbonate |
| Manufacturer: | Nexus Resin Group, LLC. |
| Trademark: | NEXUS PC |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | og8UIt_NEXUS-PC-PC1212R.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Molding Grade PC With Release |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.20 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (300°C/1.2 kg) | 12 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow | 0.50 to 0.70 | % | ASTM D955 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 2380 | MPa | ASTM D638 |
| Tensile Strength (Yield) | 58.6 | MPa | ASTM D638 |
| Flexural Modulus | 2380 | MPa | ASTM D790 |
| Flexural Strength (Yield) | 86.2 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C, 3.18 mm) | 640 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed, 3.18 mm) | 127 | °C | ASTM D648 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 121 | °C | |
| Drying Time | 4.0 | hr | |
| Suggested Max Moisture | 0.020 | % | |
| Rear Temperature | 271 to 288 | °C | |
| Middle Temperature | 277 to 299 | °C | |
| Front Temperature | 288 to 316 | °C | |
| Nozzle Temperature | 288 to 316 | °C | |
| Processing (Melt) Temp | 288 to 316 | °C | |
| Mold Temperature | 76.7 to 104 | °C | |
| Back Pressure | 0.345 to 0.689 | MPa | |
| Screw Speed | 40 to 75 | rpm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Reslen PPH 10K | Polimarky Spolka Jawna | PP Homopolymer | Reslen |
| APEX® RE 8003 | Teknor Apex Company | PVC, Rigid | APEX® |
| Durethan® BKV 140 DUS008 000000 | LANXESS GmbH | Nylon 6 | Durethan® |
| Hifax BR 713 N | LyondellBasell Industries | PP Copolymer | Hifax |
| 3M™ Dyneon™ PTFE Compound TF 7196 | 3M Advanced Materials Division | PTFE | 3M™ Dyneon™ PTFE Compound |