Sarlink® TPV 4165
| Category: | TPV , Thermoplastic Vulcanizate |
| Manufacturer: | Teknor Apex Company |
| Trademark: | Sarlink® TPV |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | oeRro8_Sarlink-TPV-4165.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| SARLINK® 4000 series are engineered materials designed primarily for demanding automotive applications. Available in both black and natural, SARLINK® 4165N exhibits excellent compression set and flex fatigue, high and low temperature performance. The material can be processed by injection molding, blow molding and extrusion for applications such as seals, gaskets, chemical resistant hose and tube, boots and bellows. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | |||
| -- | 0.958 | g/cm³ | ASTM D792 |
| -- | 0.960 | g/cm³ | ISO 1183 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness | ASTM D2240, ISO 868 | ||
| Shaw A, 5 seconds, extruded | 63 | ASTM D2240, ISO 868 | |
| Shore A, 5 seconds, injection molding | 65 | ASTM D2240, ISO 868 |
| Elastomers | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress | |||
| Transverse flow : 100% strain | 2.50 | MPa | ASTM D412, ISO 37 |
| Flow : 100% strain | 4.20 | MPa | ISO 37, ASTM D412 |
| Tensile Stress | ASTM D412, ISO 37 | ||
| Transverse flow : Fracture | 6.80 | MPa | ASTM D412, ISO 37 |
| Flow : Fracture | 5.80 | MPa | ASTM D412, ISO 37 |
| Tensile Elongation | ASTM D412, ISO 37 | ||
| Transverse flow : Fracture | 570 | % | ASTM D412, ISO 37 |
| Flow : Fracture | 280 | % | ASTM D412, ISO 37 |
| Tear Strength - Across Flow | |||
| -- | 29 | kN/m | ASTM D624 |
| -- 1 | 29 | kN/m | ISO 34-1 |
| Compression Set | ASTM D395, ISO 815 | ||
| 23°C, 22 hr | 17 | % | ASTM D395, ISO 815 |
| 70°C, 22 hr | 27 | % | ASTM D395, ISO 815 |
| 125°C, 70 hr | 40 | % | ASTM D395, ISO 815 |
| Aging | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Change in Tensile Strength in Air - Across Flow | |||
| 135°C, 1000 hr | -9.0 | % | ISO 188, ASTM D573 |
| 150°C, 168 hr | -11 | % | ASTM D573, ISO 188 |
| 100% strain 150°C, 168 hr | 0.0 | % | ISO 188, ASTM D573 |
| 100% strain 150°C, 1000 hr | 4.0 | % | ISO 188, ASTM D573 |
| Changes in tensile stress upon fracture in air- Transverse flow | |||
| 135°C, 1000 hr | -8.0 | % | ASTM D573, ISO 188 |
| 150°C, 168 hr | -11 | % | ISO 188, ASTM D573 |
| Change in Shore Hardness in Air | |||
| Support a, 135°C, 1000 hr | 2.0 | ASTM D573, ISO 188 | |
| Support a, 150°C, 168 hr | 2.0 | ISO 188, ASTM D573 | |
| Change in Volume (125°C, 70 hr, in IRM 903 Oil) | 83 | % | ASTM D471, ISO 1817 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| RTI Elec | 100 | °C | UL 746 |
| RTI Imp | 65.0 | °C | UL 746 |
| RTI | 100 | °C | UL 746 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating (1.00 mm, All Colors) | HB | UL 94 |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Apparent Shear Viscosity - Capillary, @ 206/s | |||
| 200°C | 340 | Pa·s | ASTM D3835 |
| 200°C | 340 | Pa·s | ISO 11443 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Rear Temperature | 180 - 215 | °C | |
| Middle Temperature | 180 - 215 | °C | |
| Front Temperature | 180 - 215 | °C | |
| Nozzle Temperature | 187 - 220 | °C | |
| Processing (Melt) Temp | 185 - 220 | °C | |
| Mold Temperature | 10.0 - 55.0 | °C | |
| Back Pressure | 0.100 - 1.00 | MPa | |
| Screw Speed | 100 - 200 | rpm |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Cylinder Zone 1 Temp. | 180 - 200 | °C | |
| Cylinder Zone 2 Temp. | 180 - 205 | °C | |
| Cylinder Zone 3 Temp. | 187 - 210 | °C | |
| Cylinder Zone 4 Temp. | 187 - 210 | °C | |
| Melt Temperature | 195 - 215 | °C | |
| Die Temperature | 195 - 215 | °C | |
| Take-Off Roll | 20.0 - 50.0 | °C |
| Extrusion instructions |
|---|
| Screen Pack: 20 to 60 meshScrew: general purposeCompression Ratio: 3:1 |
| Note Message | |
|---|---|
| 1 . | Method B, right-angle specimen (without cut) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| REPOL® AM650N | Reliance Industries Limited | PP Homopolymer | REPOL® |
| ULTEM™ HU1000E resin | SABIC Innovative Plastics | PEI | ULTEM™ |
| BMC 600 | Bulk Molding Compounds, Inc. | Polyester, TS | BMC |
| CYCOLOY™ CP8320 resin | SABIC Innovative Plastics Europe | PC+ABS | CYCOLOY™ |
| FRAGOM PR/900 | Crosspolimeri S.p.A. | Polyolefin, Unspecified | FRAGOM |