MBA PP 2131 70/05
| Category: | PP Copolymer , Polypropylene Copolymer |
| Manufacturer: | MBA Polymers |
| Trademark: | MBA PP |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | odiibV_MBA-PP-2131-70-05.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| A post-consumer recycled polypropylene copolymer for general use. Available in mouse grey (reference 70/05). |
| General Information | |
|---|---|
| Recycled Content |
|
| Features |
|
| Uses |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.920 | g/cm³ | Internal Method |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 8.0 | g/10 min | ISO 1133 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus (23°C) | 1450 | MPa | ISO 527-2/1 |
| Tensile Stress (Yield, 23°C) | 26.0 | MPa | ISO 527-2/50 |
| Flexural Modulus (23°C) | 1550 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 5.0 | kJ/m² | ISO 179/1eA |
| Notched Izod Impact Strength (23°C) | 5.5 | kJ/m² | ISO 180/1A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Vicat Softening Temperature | 80.0 | °C | ISO 306/B50 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 | °C | |
| Drying Time | 1.0 to 2.0 | hr | |
| Suggested Max Moisture | 0.050 to 0.10 | % | |
| Processing (Melt) Temp | 190 to 220 | °C | |
| Mold Temperature | 30.0 to 60.0 | °C |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 | °C | |
| Drying Time | 1.0 to 2.0 | hr | |
| Suggested Max Moisture | 0.050 to 0.10 | % | |
| Melt Temperature | 180 to 210 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Ateva® 1609 | Celanese EVA Performance Polymers | EVA | Ateva® |
| DESLOY™ DSC892C | DESCO Co., Ltd. | PC+ABS | DESLOY™ |
| ICORENE® Foam Products | ICO Polymers NA, A Division of A. Schulman | PE, Unspecified | ICORENE® |
| LNP™ THERMOCOMP™ RF00ASXZ compound | SABIC Innovative Plastics | Nylon 66 | LNP™ THERMOCOMP™ |
| Osterlene® MIPS131.4 | Osterman & Company | PS (MIPS) | Osterlene® |