Huafon JF-P-9980 / JF-I-9422
| Category: | PUR-Ester , Polyurethane (Polyester based) |
| Manufacturer: | Huafon Group Co., Ltd. |
| Trademark: | Huafon |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | ocuc2v_Huafon-JF-P-9980-JF-I-9422.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Characteristics: Low density. high hardness. Applications: For sandals. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Forms |
|
| Physical | Nominal Value | Unit | |
|---|---|---|---|
| Density 1 | 0.350 to 0.400 | g/cm³ |
| Hardness | Nominal Value | Unit | |
|---|---|---|---|
| Hardness | |||
| JIS Sponge A : 23°C | 60.0 to 70.0 | ||
| JIS Sponge C : 23°C | 75.0 to 85.0 |
| Thermoset | Nominal Value | Unit | |
|---|---|---|---|
| Thermoset Components | |||
| Part A | Mix Ratio by Weight: 100 | ||
| Part B | Mix Ratio by Weight: 95 to 98 |
| Uncured Properties | Nominal Value | Unit | |
|---|---|---|---|
| Color | |||
| -- 2 | Clear/Transparent | ||
| -- 3 | White | ||
| Density | |||
| 40°C 4 | 1.14 to 1.18 | g/cm³ | |
| 40°C 5 | 1.18 to 1.20 | g/cm³ | |
| Viscosity | |||
| 40°C 6 | 0.10 to 0.30 | Pa·s | |
| 40°C 7 | 2.0 to 3.0 | Pa·s |
| Cured Properties | Nominal Value | Unit | |
|---|---|---|---|
| Tensile Strength | > 4.00 | MPa | |
| Tensile Elongation at Break | > 200 | % | |
| Tear Strength | > 15.0 | kN/m |
| Note Message | |
|---|---|
| 1 . | Molded Density |
| 2 . | Part B |
| 3 . | Part A |
| 4 . | Part A |
| 5 . | Part B |
| 6 . | Part B |
| 7 . | Part A |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| DELOXEN 2010 | Vamp Tech | PPE+PS | DELOXEN |
| Flontech® FT-1-6 | Guarniflon S.p.A. - Flontech Division | PTFE | Flontech® |
| G-PAEK™ 1120FE | Gharda Chemicals Ltd. | PEK | G-PAEK™ |
| K-PU 7765 | Technovinyl Polymers India Ltd. | TPU, Unspecified | K-PU |
| LEXAN™ SLX9271T resin | SABIC Innovative Plastics | PC | LEXAN™ |