AvaSpire® AV-722 CF30
| Category: | PAEK , Polyaryletherketone |
| Manufacturer: | Solvay Specialty Polymers |
| Trademark: | AvaSpire® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | ocuVa3_AvaSpire-AV-722-CF30.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| AvaSpire AV-722 CF30 is a AvaSpire AV-722 30% carbon fiber reinforced brand. Compared with 30% carbon fiber reinforced PEEK, the components are more economical while maintaining the high performance advantages of carbon fiber reinforced PEEK. These useful properties include chemical resistance, fatigue resistance and long-term thermal oxidation stability. The excellent balance of AV-722 CF30 performance makes it available for a wide range of uses in all walks of life, including healthcare, transportation, electronics and chemical processing. The melt processability of AV-722 CF30 is very close to that of 30% CF-enhanced PEEK. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| RoHS Compliance |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.42 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (400°C/2.16 kg) | 0.80 | g/10 min | ASTM D1238 |
| Molding Shrinkage 1 | ASTM D955 | ||
| Flow : 3.18mm | 0.0 - 0.20 | % | ASTM D955 |
| Transverse flow : 3.18mm | 1.4 - 1.6 | % | ASTM D955 |
| Water Absorption (24 hr) | 0.10 | % | ASTM D570 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (M-Scale) | 107 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 2 | 22000 | MPa | ASTM D638 |
| -- | 26600 | MPa | ISO 527-2/1A/1 |
| Tensile Stress | |||
| Yield | 224 | MPa | ISO 527-2/1A/5 |
| -- 3 | 200 | MPa | ASTM D638 |
| Tensile Elongation | |||
| Fracture 4 | 1.5 | % | ASTM D638 |
| Fracture | 1.5 | % | ISO 527-2/1A/5 |
| Flexural Modulus | |||
| -- | 19300 | MPa | ASTM D790 |
| -- | 25000 | MPa | ISO 178 |
| Flexural Strength | |||
| -- | 304 | MPa | ASTM D790 |
| -- | 334 | MPa | ISO 178 |
| Compressive Strength | 170 | MPa | ASTM D695 |
| Shear Strength | 98.0 | MPa | ASTM D732 |
| Poisson's Ratio | 0.44 | ASTM E132 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | |||
| -- | 53 | J/m | ASTM D256 |
| -- | 8.5 | kJ/m² | ISO 180 |
| Unnotched Izod Impact | |||
| -- | 530 | J/m | ASTM D4812 |
| -- | 39 | kJ/m² | ISO 180 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Annealed) | 276 | °C | ASTM D648 |
| Glass Transition Temperature | 150 | °C | ASTM D3418 |
| Peak Melting Temperature 5 | 340 | °C | ASTM D3418 |
| CLTE - Flow (-50 to 50°C) | 6.0E-6 | cm/cm/°C | ASTM E831 |
| Specific Heat | DSC | ||
| 50°C | 1280 | J/kg/°C | DSC |
| 200°C | 1740 | J/kg/°C | DSC |
| Thermal Conductivity | 0.34 | W/m/K | ASTM C177 |
| Fill Analysis | Nominal Value | Unit | |
|---|---|---|---|
| Melt Viscosity (400°C, 1000 sec^-1) | 470 | Pa·s |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 149 | °C | |
| Drying Time | 4.0 | hr | |
| Rear Temperature | 366 | °C | |
| Middle Temperature | 371 | °C | |
| Front Temperature | 377 | °C | |
| Nozzle Temperature | 382 | °C | |
| Mold Temperature | 177 - 204 | °C | |
| Injection Rate | Fast | ||
| Screw Compression Ratio | 2.5:1.0 - 3.5:1.0 |
| Injection instructions |
|---|
| 保压压力：最低值 |
| Note Message | |
|---|---|
| 1 . | 5" x 0.5" x 0.125" bars |
| 2 . | 5.0 mm/min |
| 3 . | 5.0 mm/min |
| 4 . | 5.0 mm/min |
| 5 . | For main components |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Vital-Line SHE1004X | Teknor Apex Asia Pacific PTE. LTD. | PVC, Flexible | Vital-Line |
| BJB Polyurethane TC-995 A/B | BJB Enterprises, Inc. | TSU | BJB Polyurethane |
| FORMULA P COMP 3240 | Putsch Kunststoffe GmbH | PP, Unspecified | FORMULA P |
| Hifax TRC 770P G64 Gray | LyondellBasell Industries | TPO (POE) | Hifax |
| SQUARE® LIM8620-70A/B | Shenzhen SQUARE Silicone Co., Ltd. | Silicone Rubber, LSR | SQUARE® |