LNP™ LUBRICOMP™ OCL36 compound
| Category: | PPS, Linear , Linear Polyphenylene Sulfide |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | LNP™ LUBRICOMP™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | ocfYGP_LNPLUBRICOMPOCL36compound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP LUBRICOMP* OCL36 is a compound based on PPS - Linear resin containing Carbon Fiber, PTFE. Added features of this material include: Electrically Conductive. Also known as: LNP* LUBRICOMP* Compound OCL-4036 Product reorder name: OCL36 |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.52 | g/cm³ | ASTM D792, ISO 1183 |
| Molding Shrinkage | |||
| Flow : 24 hours | 0.040 - 0.10 | % | ASTM D955 |
| Transverse flow : 24 hours | 0.30 - 0.40 | % | ASTM D955 |
| Vertical flow direction : 24 hours | 0.36 - 0.40 | % | ISO 294-4 |
| Flow direction : 24 hours | 0.040 - 0.10 | % | ISO 294-4 |
| Water Absorption (Equilibrium, 23°C, 50% RH) | 0.031 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 21500 | MPa | ASTM D638 |
| -- | 30700 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Fracture | 169 | MPa | ASTM D638 |
| Fracture | 167 | MPa | ISO 527-2 |
| Tensile Elongation | |||
| Fracture | 1.4 | % | ASTM D638 |
| Fracture | 1.1 | % | ISO 527-2 |
| Flexural Modulus | 21100 | MPa | ASTM D790, ISO 178 |
| Flexural Strength | |||
| -- | 259 | MPa | ASTM D790 |
| -- | 262 | MPa | ISO 178 |
| Coefficient of Friction | ASTM D3702 Modified | ||
| With self-dynamics | 0.39 | ASTM D3702 Modified | |
| With Self-Static | 0.34 | ASTM D3702 Modified | |
| Wear Factor - Washer | 19.0 | 10^-10 in^5-min/ft-lb-hr | ASTM D3702 Modified |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | |||
| 23°C | 59 | J/m | ASTM D256 |
| 23°C 2 | 6.3 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact | |||
| 23°C | 440 | J/m | ASTM D4812 |
| 23°C 3 | 31 | kJ/m² | ISO 180/1U |
| Instrumented Dart Impact | |||
| 23°C, Energy at Peak Load | 15.1 | J | ASTM D3763 |
| -- | 2.97 | J | ISO 6603-2 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 1.8 MPa, unannealed, 3.20mm | 267 | °C | ASTM D648 |
| 1.8 MPa, unannealed, 64.0mm span 4 | 263 | °C | ISO 75-2/Af |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 121 - 149 | °C | |
| Drying Time | 4.0 | hr | |
| Rear Temperature | 304 - 316 | °C | |
| Middle Temperature | 321 - 332 | °C | |
| Front Temperature | 332 - 343 | °C | |
| Processing (Melt) Temp | 316 - 321 | °C | |
| Mold Temperature | 138 - 166 | °C | |
| Back Pressure | 0.172 - 0.344 | MPa | |
| Screw Speed | 30 - 60 | rpm |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | 80*10*4 |
| 3 . | 80*10*4 |
| 4 . | 80*10*4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Vydyne® 41H NT | Ascend Performance Materials Operations LLC | Nylon 66 | Vydyne® |
| WPP PP PPH4CF-4 | Washington Penn Plastic Co. Inc. | PP Homopolymer | WPP PP |
| Elastane™ 4721R10 | Technical Polymers, LLC | TPU-Polyester | Elastane™ |
| Keltan® ECO 9950 | LANXESS Buna GmbH | EPDM | Keltan® |
| Sylvin 8353-98FUV White 1513 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |