MAJORIS EE097 - 7803
| Category: | PP, Unspecified , Polypropylene |
| Manufacturer: | AD majoris |
| Trademark: | MAJORIS |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | ocVtA7_MAJORIS-EE097---7803.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
EE097 - 7803 is a 8 % mineral filled polypropylene compound intended for injection moulding. EE097 - 7803 has been developed especially for the automotive parts, requiring good impact strength/stiffness, very good scratch resistance and UV stabilised. The product is available in natural (EE097) but other colours can be provided on request. APPLICATIONS
|
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Uses |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.953 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 12 | g/10 min | ISO 1133 |
| Molding Shrinkage | 1.2 | % |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 1750 | MPa | ISO 527-2/1 |
| Tensile Stress (Yield) | 21.0 | MPa | ISO 527-2/50 |
| Tensile Strain (Yield) | 6.0 | % | ISO 527-2/50 |
| Flexural Modulus 1 | 1600 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | ||
| -20°C | 5.0 | kJ/m² | ISO 179/1eA |
| 23°C | 21 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength | ISO 179/1eU | ||
| -20°C | 62 | kJ/m² | ISO 179/1eU |
| 23°C | 170 | kJ/m² | ISO 179/1eU |
| Notched Izod Impact | ISO 180/1A | ||
| 0°C | 6.0 | kJ/m² | ISO 180/1A |
| 23°C | 26 | kJ/m² | ISO 180/1A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, not annealed | 100 | °C | ISO 75-2/B |
| 1.8 MPa, not annealed | 55.0 | °C | ISO 75-2/A |
| Vicat Softening Temperature | |||
| -- | 136 | °C | ISO 306/A |
| -- | 54.0 | °C | ISO 306/B |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 | °C | |
| Drying Time | 3.0 | hr | |
| Processing (Melt) Temp | 220 - 260 | °C | |
| Mold Temperature | 30.0 - 50.0 | °C | |
| Injection Rate | Moderate |
| Injection instructions |
|---|
| Holding pressure: 50 to 70% of the injection pressure |
| Note Message | |
|---|---|
| 1 . | 2.0 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Maxelast® P1855 | Nantong Polymax Elastomer Technology, Co., Ltd | TPE | Maxelast® |
| Medalist® MD-325 | Teknor Apex Company | TPE | Medalist® |
| FHR Polypropylene P4C6B-194 | Flint Hills Resources, LP | PP Homopolymer | FHR Polypropylene |
| Shida 3210 | JINJIANG City SHIDA Plastic Fine Co., Ltd. | TPE | Shida |
| LNP™ STAT-KON™ DD0001 compound | SABIC Innovative Plastics | PC | LNP™ STAT-KON™ |