LUVOCOM® 6-8512 Datasheet,Nylon 12,LEHVOSS Group-SHANGHAI SUSHENG

Message
LUVOCOM®6-8512 is a polyamide 12 (nylon 12) material, and the filler is carbon fiber reinforced material. This product is available in North America, Africa and the Middle East, Latin America, Europe or Asia Pacific,. LUVOCOM®The main features of 6-8512 are: Good dimensional stability moisture resistance Wear-resistant Lubrication Typical application areas include: engineering/industrial accessories textile/fiber Automotive Industry business/office supplies Handle

General Information
Filler / Reinforcement	Carbon fiber reinforced material
Additive	Lubricant
Features	Good dimensional stability Low friction coefficient Good wear resistance Lubrication Low or no water absorption
Uses	Handle Textile applications Engineering accessories Machine/mechanical parts Application in Automobile Field Business equipment Bearing
Appearance	Dark gray

Physical	Nominal Value	Unit	Test Method
Density	1.10	g/cm³	ISO 1183
Melt Volume-Flow Rate (MVR) (250°C/2.16 kg)	3.00	cm³/10min	ISO 1133
Molding Shrinkage	0.40 - 0.80	%	DIN 16901
Water Absorption (23°C, 24 hr)	< 0.10	%

Mechanical	Nominal Value	Unit	Test Method
Tensile Modulus	3500	MPa	ISO 527-2
Tensile Stress (Break)	60.0	MPa	ISO 527-2
Tensile Strain (Yield)	5.0	%	ISO 527-2
Flexural Modulus	3000	MPa	ISO 178
Flexural Stress	90.0	MPa	ISO 178
Flexural Strain at Flexural Strength	7.0	%	ISO 178

Thermal	Nominal Value	Unit	Test Method
Maximum operating temperature- Short Term	140	°C

Electrical	Nominal Value	Unit	Test Method
Insulation Resistance	> 1.0E+11	ohms	IEC 60167

Impact	Nominal Value	Unit	Test Method
Charpy Unnotched Impact Strength (23°C)	70	kJ/m²	ISO 179/1fU

Thermal	Nominal Value	Unit	Test Method
Continuous Use Temperature	90.0	°C	UL 746B

Electrical	Nominal Value	Unit	Test Method
Surface Resistivity	> 1.0E+11	ohms	IEC 60093

Injection	Nominal Value	Unit
Drying Temperature
Hot air dryer, A	75	°C
Hot air dryer, B	105	°C
Drying Time
Hot air dryer, A	6.0 - 10	hr
Hot air dryer, B	< 4.0	hr
Rear Temperature	230 - 250	°C
Middle Temperature	240 - 260	°C
Front Temperature	250 - 270	°C
Nozzle Temperature	250 - 260	°C
Processing (Melt) Temp	250	°C
Mold Temperature	70 - 110	°C

Injection instructions
General In general LUVOCOM® can be processed on conventional injection moulding machines while observing the usual technical guidelines. Any added fibrous materials or fillers may have an abrasive effect. In this case the cylinder and screw should be protected against wear as is usual in the processing of reinforced thermoplastic materials. Lengthy dwell times for the melts in the cylinder should be avoided. Lower the temperatures during interruptions! Predrying (optional) It is advisable to predry the granulate with a suitable dryer immediately before processing. The granulate may absorb moisture from the air. Delivery Form & Storage Unless indicated otherwise, the material is delivered as 3mm-long pellets in sealed bags on pallets. Preferably storage should be effected in dry and normally temperatured rooms Additional Information During processing the moisture level should not exceed 0.1%, otherwise molecular degradation and surface defects (e.g. smearing) may occur. As the material absorbs water rapidly, originally sealed containers should only be opened immediately before processing. Excessively high predrying temperatures may cause discoloration. The processing notes provided merely represent a recommendation for general use. Due to the large variety of machines, geometries and volumes of parts, etc., it may be necessary to employ different settings according to the specific application. Please contact us for further information.

Injection instructions

General In general LUVOCOM® can be processed on conventional injection moulding machines while observing the usual technical guidelines. Any added fibrous materials or fillers may have an abrasive effect. In this case the cylinder and screw should be protected against wear as is usual in the processing of reinforced thermoplastic materials. Lengthy dwell times for the melts in the cylinder should be avoided. Lower the temperatures during interruptions! Predrying (optional) It is advisable to predry the granulate with a suitable dryer immediately before processing. The granulate may absorb moisture from the air. Delivery Form & Storage Unless indicated otherwise, the material is delivered as 3mm-long pellets in sealed bags on pallets. Preferably storage should be effected in dry and normally temperatured rooms Additional Information During processing the moisture level should not exceed 0.1%, otherwise molecular degradation and surface defects (e.g. smearing) may occur. As the material absorbs water rapidly, originally sealed containers should only be opened immediately before processing. Excessively high predrying temperatures may cause discoloration. The processing notes provided merely represent a recommendation for general use. Due to the large variety of machines, geometries and volumes of parts, etc., it may be necessary to employ different settings according to the specific application. Please contact us for further information.

Category:	Nylon 12 , Polyamide 12
Manufacturer:	LEHVOSS Group
Trademark:	LUVOCOM®
Fillers:	-
Ports:	Qinzhou, Shekou, Shanghai, Ningbo
Delivery Terms	FOB, CIF, DAP, DAT, DDP
PDF:	oYntWW_LUVOCOM68512.pdf
PRICE:	Order Products email sales@su-jiao.com

Resin Grade	Manufacturer	Category	Trademark
Shandong Nylon A1L04	Shandong Dongchen Engineering Plastics Co., Ltd.	Nylon, Unspecified	Shandong Nylon
Tecodur® PB70 GB30 NL	Eurotec Engineering Plastics	PBT	Tecodur®
SPESIN® KP212G30V0HI	Kolon Plastics, Inc.	PBT	SPESIN®
EVICOM™ GA4/155	INEOS Compounds	PVC, Flexible	EVICOM™
DuraSurf™ Galleria	Crown Plastics	UHMWPE	DuraSurf™