XYCOMP® 5101
| Category: | PEEK , Polyetheretherketone |
| Manufacturer: | Greene, Tweed & Co. |
| Trademark: | XYCOMP® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | oYBWyg_XYCOMP-5101.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| XYCOMP® 5101 is a Polyetheretherketone (PEEK) product filled with carbon fiber. It is available in Europe or North America. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Appearance |
|
| Forms |
|
| Mechanical | Nominal Value | Unit | |
|---|---|---|---|
| Tensile Modulus | |||
| 23°C 1 | 10300 | MPa | |
| 23°C | 138000 | MPa | |
| 82°C 2 | 9650 | MPa | |
| 82°C 3 | 138000 | MPa | |
| Tensile Strength | |||
| Break, 23°C 4 | 89.6 | MPa | |
| Break, 23°C | 2070 | MPa | |
| Break, 82°C 5 | 82.7 | MPa | |
| Break, 82°C 6 | 2030 | MPa | |
| Tensile Elongation | |||
| Break, 23°C 7 | 0.88 | % | |
| Break, 23°C | 1.5 | % | |
| Break, 82°C 8 | 0.86 | % | |
| Flexural Modulus | |||
| 23°C | 124000 | MPa | |
| 82°C 9 | 124000 | MPa | |
| Flexural Strength | |||
| 23°C | 2000 | MPa | |
| 82°C 10 | 1860 | MPa | |
| Compressive Modulus 11 | 124000 | MPa | |
| Compressive Strength | |||
| 82°C 12 | 1240 | MPa | |
| 23°C | 1360 | MPa | |
| Shear Modulus | |||
| -- 13 | 5100 | MPa | |
| -- 14 | 5650 | MPa | |
| Shear Strength | |||
| 23°C | 186 | MPa | |
| 82°C 15 | 165 | MPa | |
| Poisson's Ratio 16 | 0.30 | ||
| Compressive Strength - Open Hole | |||
| 23°C | 324 | MPa | |
| 82°C 17 | 283 | MPa | |
| Tensile Strength - Open Hole (23°C) | 386 | MPa |
| Additional Information | Nominal Value | Unit | |
|---|---|---|---|
| Toughness Properties | |||
| Compression after Impact 18 | 338 | MPa | |
| Mode I G1c : 23°C | 1.70 | kJ/m² | |
| Mode II G1c : 23°C 19 | 2.00 | kJ/m² |
| Note Message | |
|---|---|
| 1 . | 90° |
| 2 . | 90°, Wet |
| 3 . | Wet |
| 4 . | 90° |
| 5 . | 90°, Wet |
| 6 . | Wet |
| 7 . | 90° |
| 8 . | 90°, Wet |
| 9 . | Wet |
| 10 . | Wet |
| 11 . | 180°F, Wet |
| 12 . | Wet |
| 13 . | 180°F, Wet |
| 14 . | 73°F |
| 15 . | Wet |
| 16 . | 73°F |
| 17 . | Wet |
| 18 . | Strength after 1500 in-lb/in impact |
| 19 . | Interlaminar Fracture |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| MAXAMID™ PA66-8018-BK | Pier One Polymers, Inc. | Nylon 66 | MAXAMID™ |
| ALTECH® PP-H A 2030/250 GF30 CP | ALBIS PLASTIC GmbH | PP Homopolymer | ALTECH® PP-H |
| PENTAMID B E20X H natur | PENTAC Polymer GmbH | Nylon 6 | PENTAMID B |
| WELLAMID Nylon 6600/58 GV 15 HWCP | CP-Polymer-Technik GmbH & Co. KG | Nylon 66 | WELLAMID Nylon |
| SABIC® FORTIFY™ C1085 | Saudi Basic Industries Corporation (SABIC) | TPO (POE) | SABIC® FORTIFY™ |