Borealis PP HH315MO
| Category: | PP Homopolymer , Polypropylene Homopolymer |
| Manufacturer: | Borealis AG |
| Trademark: | Borealis PP |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | oUR1zN_Borealis-PP-HH315MO.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
HH315MO is a polypropylene homopolymer intended for injection moulding. Its high melt flow makes it especially suitable for products with long flow length. This grad is designed for high-speed injection moulding and contains nucleating, antistatic and slip additives. This polymer is a CR (controlled rheology) grade with narrow molecular weight distribution giving low warpage. Products originating from this grade have excellent demoulding properties, very high stiffness, good transparency and gloss and good impact strength at ambient temperatures. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.910 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 35 | g/10 min | ISO 1133 |
| Molding Shrinkage | 1.0 to 2.0 | % |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 102 | ISO 2039-2 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 1650 | MPa | ISO 527-2/1 |
| Tensile Stress (Yield) | 36.0 | MPa | ISO 527-2/50 |
| Tensile Strain (Yield) | 8.0 | % | ISO 527-2/50 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 2.5 | kJ/m² | ISO 179/1eA |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature 1(0.45 MPa, Unannealed) | 105 | °C | ISO 75-2/B |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Processing (Melt) Temp | 210 to 250 | °C | |
| Mold Temperature | 15.0 to 60.0 | °C | |
| Injection Rate | Fast | ||
| Holding Pressure | 20.0 to 50.0 | MPa |
| Note Message | |
|---|---|
| 1 . | Injection molded specimen |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SITRALAC S20 black | SITRAPLAS GmbH | ABS | SITRALAC |
| ACLAR® Flex 250 | Honeywell | PCTFE | ACLAR® |
| Clariant Nylon 6/6 PA-113G33C | Clariant Corporation | Nylon 66 | Clariant Nylon 6/6 |
| Haysite Plastics HCR-125 | Haysite Reinforced Plastics | Vinyl Ester | Haysite Plastics |
| LOTTMER HX-064AN | Lotte Chemical Corporation | TPE | LOTTMER |