Tuftec™ H1062
| Category: | SEBS , Styrene Ethylene Butylene Styrene Block Copolymer |
| Manufacturer: | AKelastomers |
| Trademark: | Tuftec™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | oTMNeV_Tuftec-H1062.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Specially designed for modification of polypropylene (PP), as a reinforcing agent that imparts high impact strength without significantly decreasing its rigidity, and also for increasing its elongation and low-temperature brittleness resistance to levels that are unattainable with olefinic elastomers. Also highly compatible with olefinic elastomers, enabling co-use. It is supplied in pellet form. Primarily as modifier of PP for automotive exteriors and interiors, but also effective as modifier of PP for other applications, particularly those requiring elongation and low-temperature performance, as base polymer of SEBS compounds, and as adhesives and sealants component. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 17 | g/10 min | ASTM D1238 |
| Bound Styrene | 18.0 | % | Internal method |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness | 60 | ISO 2039-2 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 1 | 18.0 | MPa | ASTM D638 |
| Tensile Elongation 2(Break) | 470 | % | ASTM D638 |
| Flexural Modulus 3 | 1820 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C, 0.125 mm) | 650 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (0.45 MPa, Unannealed) | 106 | °C | ASTM D648 |
| Brittleness Temperature | -32.3 | °C | ASTM D746 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Rear Temperature | 230 | °C | |
| Middle Temperature | 230 | °C | |
| Front Temperature | 230 | °C | |
| Mold Temperature | 40.0 | °C |
| Injection instructions |
|---|
| Injection Time: 10 secCooling Time: 30 sec |
| Note Message | |
|---|---|
| 1 . | 20 mm/min |
| 2 . | 20 mm/min |
| 3 . | 2.0 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Manner Flexible PVC V824-1 | Manner Plastics, L.P. | PVC, Flexible | Manner Flexible PVC |
| DAI-EL™ G-752 | DAIKIN AMERICA, INC. | Fluorelastomer | DAI-EL™ |
| HIFOR Xtreme® SC74853 | Westlake Chemical Corporation | LLDPE | HIFOR Xtreme® |
| Karina IVORY PVC COMPOUND 90900-35/1-Y-IS-SD | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| Delene 3550 | Shanghai Lin Gen Rubber Materials Co., Ltd. | TPE | Delene |