DOWLEX™ 3010

Category:	LLDPE , Polyethylene Resin
Manufacturer:	The Dow Chemical Company
Trademark:	DOWLEX™
Fillers:	-
Ports:	Qinzhou, Shekou, Shanghai, Ningbo
Delivery Terms	FOB, CIF, DAP, DAT, DDP
PDF:	oTEq2y_DOWLEX-3010.pdf
PRICE:	Order Products email sales@su-jiao.com

Wechat: WECHAT

WECHAT

Message

DOWLEX™ 3010 Polyethylene Resin is a polyethylene polymer designed to offer high performance properties such as excellent Environmental Stress Crack Resistance (ESCR), tear strength, abrasion resistance, and strong heat seals in thin extrusion coatings.

Linear Low Density Polyethylene

For flexible packaging, overwraps and lamination applications

Complies with:

U.S. FDA 21 CFR 177.1520 (c)

Canadian HPFB No Objection (With Limitations)

EU, No 10/2011

Japan Hygienic Styrene Plastics Association

This resin may be used to manufacture articles for use in packing or holding food during cooking. This statement refers to the extraction limitations only, not to the product's physical utility.

Consult the regulations for complete details.

General Information
Agency Ratings	FDA 21 CFR 177.1520(c) HPFB (Canada) No Objection 2 JHOSPA not rated Europe No 10/2011
Forms	Particle
Processing Method	Extrusion coating

Physical	Nominal Value	Unit	Test Method
Specific Gravity	0.921	g/cm³	ASTM D792
Melt Mass-Flow Rate (MFR) (190°C/2.16 kg)	5.4	g/10 min	ASTM D1238

Mechanical	Nominal Value	Unit	Test Method
Coefficient of Friction ¹(vs. Itself - Dynamic)	0.60		ASTM D1894

Films	Nominal Value	Unit	Test Method
Seal Initiation Temperature ²	115	°C	Internal method
Water Vapor Transmission Rate ³	0.63	g·mm/m²/atm/24 hr	ASTM F1249

Thermal	Nominal Value	Unit	Test Method
Vicat Softening Temperature	100	°C	ASTM D1525
Melting Temperature (DSC)	124	°C	Internal method

Extrusion	Nominal Value	Unit	Test Method
Melt Temperature	316 - 327	°C
Neck-in (321°C, 25.4 µm)	124.5	mm	Internal method
Maximum production line speed	8.1	m/sec	Internal method
Minimum coating thickness	7.1	µm	Internal method
Minimum coating weight	6.8	g/m²	Internal method

Extrusion instructions
挤出涂层薄膜的制造条件：螺杆尺寸：3.5" (89 mm) 30:1 L/D 螺杆类型：带 Maddock Mixer 的单跨型模具间隙：20 密尔 (0.508 mm) 熔体温度：600 °F (315 °C) 输出：250 磅/小时螺杆速度：90 rpm

Note Message
1 .	1.0 Mill (25 µm) coating applied to 50 pounds of kraft paper.
2 .	1.0 Mill (25 µm) coating applied to 50 pounds of kraft paper. Achieve a temperature of 1 psig (4.4 N/25.4mm) heat seal strength. Heat seal strength, Topwave HT tester 0.5 S pressure, 40 psi pressure, pulling speed 150 mm/s.
3 .	1.0 Mill (25 µm) coating applied to 50 pounds of kraft paper.

Resin Grade	Manufacturer	Category	Trademark
Fluoroloy® A16	Saint Gobain Performance Plastics	TP, Unspecified	Fluoroloy®
Epolene® N-30	Westlake Chemical Corporation	LDPE	Epolene®
MAJORIS G420	AD majoris	PP, Unspecified	MAJORIS
EPAMOULD 293A34	Epaflex Polyurethanes S.R.L.	TPU-Polyester	EPAMOULD
Sylvin 8784-77 White 1360	Sylvin Technologies Incorporated	PVC, Unspecified	Sylvin