Network Polymers SAN 279
| Category: | SAN , Styrene Acrylonitrile |
| Manufacturer: | Network Polymers, Inc. |
| Trademark: | Network Polymers SAN |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | oSQXX2_Network-Polymers-SAN-279.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Network Polymers SAN 279 is a Styrene Acrylonitrile (SAN) product. It can be processed by injection molding and is available in North America. Typical application: Food Contact Applications. Primary characteristic: flame rated. |
| General Information | |
|---|---|
| Agency Ratings |
|
| Appearance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.08 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) 1 | ASTM D1238 | ||
| 200°C/5.0 kg | 2.0 | g/10 min | |
| 230°C/3.8 kg | 7.5 | g/10 min | |
| Molding Shrinkage - Flow | 0.30 to 0.70 | % | ASTM D955 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 123 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 2(Yield) | 71.7 | MPa | ASTM D638 |
| Flexural Modulus - Tangent 3 | 3450 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C, 3.18 mm) | 21 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed, 3.18 mm) | 88.9 | °C | ASTM D648 |
| Vicat Softening Temperature | 101 | °C | ASTM D1525 4 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating (1.50 mm) | HB | UL 94 |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Transmittance | 89.0 | % | ASTM D1003 |
| Haze | 1.9 | % | ASTM D1003 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 71.1 to 82.2 | °C | |
| Drying Time | 2.0 to 4.0 | hr | |
| Suggested Shot Size | 40 to 75 | % | |
| Rear Temperature | 160 to 182 | °C | |
| Middle Temperature | 182 to 221 | °C | |
| Front Temperature | 193 to 232 | °C | |
| Nozzle Temperature | 193 to 232 | °C | |
| Processing (Melt) Temp | 193 to 216 | °C | |
| Mold Temperature | 26.7 to 76.7 | °C | |
| Injection Pressure | 0.414 to 7.58 | MPa | |
| Injection Rate | Moderate-Fast | ||
| Back Pressure | 0.517 to 1.03 | MPa | |
| Clamp Tonnage | 2.8 to 4.1 | kN/cm² |
| Note Message | |
|---|---|
| 1 . | Procedure A |
| 2 . | 51 mm/min |
| 3 . | 1.3 mm/min |
| 4 . | Loading 1 (10 N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SUMILITE® CEL-7040 | Sumitomo Bakelite Co., Ltd. | LLDPE | SUMILITE® |
| NEFTEKHIM PS 585 | Nizhnekamskneftekhim Inc. | PS (GPPS) | NEFTEKHIM PS |
| NOVALAC RX®525 | Vyncolit N.V. | Phenolic | NOVALAC |
| Edgetek™ ET3300-0030 RS White | PolyOne Corporation | PBT | Edgetek™ |
| Karina IVORY PVC COMPOUND -E 818-35/ 1-Y-SN-ERM | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |