LNP™ STAT-KON™ 115EM4 compound
| Category: | PPE+PS , Polyphenylene Ether + PS |
| Manufacturer: | SABIC Innovative Plastics Asia Pacific |
| Trademark: | LNP™ STAT-KON™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | oRBgqD_LNP-STAT-KON-115EM4-compound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP* STAT-KON* 115EM4 is an electrically conductive compound based on PPE+PS containing carbon powder. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.16 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow (3.20 mm) | 0.70 to 0.80 | % | Internal Method |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Yield) | 69.0 | MPa | Internal Method |
| Tensile Elongation (Break) | 6.0 | % | Internal Method |
| Flexural Modulus | 3340 | MPa | ASTM D790 |
| Flexural Strength | 108 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 49 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (0.45 MPa, Unannealed, 3.20 mm) | 163 | °C | ASTM D648 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+4 to 1.0E+6 | ohms | ASTM D257 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Ryton® R-4-220BL | Solvay Specialty Polymers | PPS | Ryton® |
| Stanyl® TE250F8 | DSM Engineering Plastics | Nylon 46 | Stanyl® |
| TAROPRENE® 1 A60 M1N | Taro Plast S.p.A. | TPV | TAROPRENE® |
| Dugdale PVC Rigid Clear Extrusion - Blue Tint Compound | Dugdale Plc | PVC, Rigid | Dugdale PVC |
| OPTODYNE™ UV-1000 | Daikin Fluorochemicals (China) Co., Ltd. | Epoxy | OPTODYNE™ |