SABIC® PPcompound 2609A
| Category: | PP, Unspecified , Polypropylene |
| Manufacturer: | Saudi Basic Industries Corporation (SABIC) |
| Trademark: | SABIC® PPcompound |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | oQxCuY_SABIC-PPcompound-2609A.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
SABIC® PPcompound 2609A is a mineral filled modified polypropylene. Typical material properties include good stiffness and impact with a low shrinkage and CLTE. Typical applications include automotive exterior trims such as lateral siding. It can be used in painted and unpainted applications with UV stabilization added on demand. SABIC® PPcompound 2609A is a designated automotive grade. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.12 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) | ISO 1133 | ||
| 230°C/2.16 kg | 15 | g/10 min | |
| 230°C/5.0 kg | 50 | g/10 min | |
| Molding Shrinkage (24 hr) | 0.70 | % | Internal Method |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Shore Hardness (Shore D, Injection Molded) | 62 | ISO 868 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress | ISO 527-2/5/50 | ||
| Yield, 3.20 mm, Injection Molded | 20.0 | MPa | |
| Break, 3.20 mm, Injection Molded | 17.0 | MPa | |
| Tensile Strain (Break, 3.20 mm, Injection Molded) | 25 | % | ISO 527-2/5/50 |
| Flexural Modulus 1(Injection Molded) | 1900 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C, Injection Molded) | 10 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength (-40°C, Injection Molded) | 15 | kJ/m² | ISO 179/1eU |
| Notched Izod Impact Strength | ISO 180/4A | ||
| -20°C, Injection Molded | 2.5 | kJ/m² | |
| 0°C, Injection Molded | 3.5 | kJ/m² | |
| 23°C, Injection Molded | 6.4 | kJ/m² |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (0.45 MPa, Unannealed) | 105 | °C | ISO 75-2/B |
| Vicat Softening Temperature | 135 | °C | ISO 306/A |
| CLTE - Flow | ASTM D696 | ||
| -30 to 30°C | 5.5E-5 | cm/cm/°C | |
| 23 to 80°C | 9.0E-5 | cm/cm/°C |
| Note Message | |
|---|---|
| 1 . | Method I (3 point load) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Maxelast® P1957TB | Nantong Polymax Elastomer Technology, Co., Ltd | TPE | Maxelast® |
| SOLLAMID A 2700 - A 2730 FV 50 | Krisoll Resinas Plásticas Ltda. | Nylon 66 | SOLLAMID |
| Baydur® 742 IBS (37 pcf) | Covestro - PUR | PUR-MDI | Baydur® |
| FHR Polypropylene P9H9Z-018 | Flint Hills Resources, LP | PP, Unspecified | FHR Polypropylene |
| LEXAN™ LUX2289 resin | SABIC Innovative Plastics | PC | LEXAN™ |