Taitalac® 5000M
| Category: | ABS , Acrylonitrile Butadiene Styrene |
| Manufacturer: | Taita Chemical Company, Ltd. |
| Trademark: | Taitalac® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | oQs9Dd_Taitalac-5000M.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Taitalac® 5000M is an Acrylonitrile Butadiene Styrene (ABS) material. It is available in Asia Pacific or North America for injection molding. Important attributes of Taitalac® 5000M are:
Typical applications include:
|
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.04 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) | ASTM D1238 | ||
| 200°C/5.0 kg | 1.8 | g/10 min | |
| 220°C/10.0 kg | 20 | g/10 min | |
| Molding Shrinkage - Flow | < 0.40 | % | ASTM D955 |
| Water Absorption (Saturation) | < 0.30 | % | ASTM D570 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale, 23°C) | 115 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 1 | ASTM D638 | ||
| Yield, 23°C, 3.18 mm | 44.1 | MPa | |
| Break, 23°C, 3.18 mm | 37.3 | MPa | |
| Tensile Elongation 2(Break, 23°C, 3.18 mm) | 30 | % | ASTM D638 |
| Flexural Modulus 3(23°C) | 27000 | MPa | ASTM D790 |
| Flexural Strength 4(Yield, 23°C) | 77.5 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | ASTM D256 | ||
| 23°C, 3.18 mm | 200 | J/m | |
| 23°C, 6.35 mm | 180 | J/m |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed, 12.7 mm) | 85.0 | °C | ASTM D648 |
| Vicat Softening Temperature 5 | 103 | °C | ASTM D1525 6 |
| RTI Elec (1.59 mm) | 60.0 | °C | UL 746 |
| RTI Imp (0.0625 mm) | 60.0 | °C | UL 746 |
| RTI Str (1.59 mm) | 60.0 | °C | UL 746 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| High Amp Arc Ignition (HAI) (0.0620 mm) | 200 | UL 746 | |
| High Voltage Arc Tracking Rate (HVTR) (0.0620 mm) | 0.00 | mm/min | UL 746 |
| Hot-wire Ignition (HWI) (1.57 mm) | 18 | sec | UL 746 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (1.59 mm) | HB | UL 94 |
| Note Message | |
|---|---|
| 1 . | 5.0 mm/min |
| 2 . | 5.0 mm/min |
| 3 . | 2.8 mm/min |
| 4 . | 2.8 mm/min |
| 5 . | 1/8 in |
| 6 . | Loading 1 (10 N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Razalen® R123 TR15 | Razin™ Engineering Plastics | PP+EPDM | Razalen® |
| Sylvin 8463-60 Black | Sylvin Technologies Incorporated | PVC+NBR | Sylvin |
| Witcom PE 4L1 | Witcom Engineering Plastics B.V. | PE, Unspecified | Witcom PE |
| ASI POLYETHYLENE CP 851 | A. Schulman Inc. | LDPE | ASI POLYETHYLENE |
| Eltex® MED 100-MG12 | INEOS Olefins & Polymers Europe | PP Homopolymer | Eltex® MED |