SUPREME HIPS SH731

Category:	PS (HIPS) , High Impact Polystyrene
Manufacturer:	Supreme Petrochem Ltd.
Trademark:	SUPREME HIPS
Fillers:	-
Ports:	Qinzhou, Shekou, Shanghai, Ningbo
Delivery Terms	FOB, CIF, DAP, DAT, DDP
PDF:	oQ3zsX_SUPREME-HIPS-SH731.pdf
PRICE:	Order Products email sales@su-jiao.com

Wechat: WECHAT

WECHAT

Message

High Impact Polystyrene (HIPS)

Characteristics:

Medium Flow

High Impact

Excellent Formability

Low Temperature Toughness

Processing:

Molding

Extrusion & Forming

Applications:

Thermoformed food & non food packaging, extruded profile

Plates, dishes, disposable cups, deep drawn thermoformed containers

Also suitable for audio/video cabinets, business machines, ball pen toys

General Information
Features	Disposable Food Contact Acceptable Good Moldability High Impact Resistance Low Temperature Toughness Medium Flow
Uses	Cups Industrial Applications Kitchenware Packaging Profiles Thermoformed Containers
Agency Ratings	FDA 21 CFR 177.1640
UL File Number	E185934
Forms	Pellets
Processing Method	Extrusion Injection Molding Thermoforming

Physical	Nominal Value	Unit	Test Method
Specific Gravity	1.30	g/cm³	ASTM D792
Melt Mass-Flow Rate (MFR) (200°C/5.0 kg)	4.5	g/10 min	ASTM D1238

Mechanical	Nominal Value	Unit	Test Method
Tensile Strength ¹(23°C, 3.20 mm, Injection Molded)	28.0	MPa	ASTM D638
Tensile Elongation ²(Break, 23°C, 3.20 mm, Injection Molded)	50	%	ASTM D638
Flexural Modulus (23°C, 3.20 mm, Injection Molded)	1900	MPa	ASTM D790
Flexural Strength (23°C, 3.20 mm, Injection Molded)	44.0	MPa	ASTM D790

Impact	Nominal Value	Unit	Test Method
Notched Izod Impact (23°C, 3.20 mm, Injection Molded)	110	J/m	ASTM D256

Thermal	Nominal Value	Unit	Test Method
Deflection Temperature Under Load (1.8 MPa, Unannealed, Injection Molded)	82.0	°C	ASTM D648
Vicat Softening Temperature	102	°C	ASTM D1525 ³

Flammability	Nominal Value		Test Method
Flame Rating (1.60 mm)	HB		UL 94

Injection	Nominal Value	Unit
Processing (Melt) Temp	180 to 260	°C
Mold Temperature	40.0 to 60.0	°C

Extrusion	Nominal Value	Unit
Melt Temperature	180 to 260	°C

Note Message
1 .	50 mm/min
2 .	50 mm/min
3 .	Rate B (120°C/h), Loading 1 (10 N)

Resin Grade	Manufacturer	Category	Trademark
Chemraz 562	Greene, Tweed & Co.	Perfluoroelastomer	Chemraz
ETILINAS PC4020	POLYETHYLENE MALAYSIA SDN BHD	MDPE	ETILINAS
K-vinyl 60 Deg C Rating Insulation (85-Wet)	Technovinyl Polymers India Ltd.	PVC, Unspecified	K-vinyl
Polimid A 50 GF	Poliblend S.p.a.	Nylon 66	Polimid A
Sylvin 9790-60 Green 3205	Sylvin Technologies Incorporated	PVC, Unspecified	Sylvin