LNP™ LUBRICOMP™ DBL32 compound
| Category: | PC , Polycarbonate |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | LNP™ LUBRICOMP™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | oPyvpA_LNPLUBRICOMPDBL32compound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP LUBRICOMP DBL32 is a compound based on Polycarbonate resin containing PTFE, Carbon Fiber. Added features of this material include: Electrically Conductive, Internally Lubricated. Also known as: LNP* LUBRICOMP* Compound DBL-4032 Product reorder name: DBL32 |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.37 | g/cm³ | ASTM D792, ISO 1183 |
| Molding Shrinkage | |||
| Flow : 24 hours | 0.70 - 0.90 | % | ASTM D955 |
| Transverse flow : 24 hours | 0.90 - 1.1 | % | ASTM D955 |
| Vertical flow direction : 24 hours | 0.96 | % | ISO 294-4 |
| Flow direction : 24 hours | 0.80 | % | ISO 294-4 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 2070 | MPa | ASTM D638 |
| -- | 2580 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Yield | 42.7 | MPa | ASTM D638 |
| Yield | 43.0 | MPa | ISO 527-2 |
| Fracture | 38.6 | MPa | ASTM D638 |
| Fracture | 38.0 | MPa | ISO 527-2 |
| Tensile Elongation | |||
| Yield | 5.4 | % | ASTM D638 |
| Yield | 5.1 | % | ISO 527-2 |
| Fracture | 22 | % | ASTM D638 |
| Fracture | 18 | % | ISO 527-2 |
| Flexural Modulus | |||
| -- | 2760 | MPa | ASTM D790 |
| -- | 2400 | MPa | ISO 178 |
| Flexural Stress | 69.0 | MPa | ISO 178 |
| Coefficient of Friction | ASTM D3702 Modified | ||
| With self-dynamics | 0.42 | ASTM D3702 Modified | |
| With Self-Static | 0.48 | ASTM D3702 Modified | |
| Wear Factor - Washer | 139 | 10^-10 in^5-min/ft-lb-hr | ASTM D3702 Modified |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | |||
| 23°C | 190 | J/m | ASTM D256 |
| 23°C 2 | 14 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact | |||
| 23°C | 1500 | J/m | ASTM D4812 |
| 23°C 3 | 110 | kJ/m² | ISO 180/1U |
| Instrumented Dart Impact | |||
| 23°C, Energy at Peak Load | 31.5 | J | ASTM D3763 |
| -- | 25.8 | J | ISO 6603-2 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, unannealed, 3.20mm | 143 | °C | ASTM D648 |
| 0.45 MPa, unannealed, 64.0mm span 4 | 139 | °C | ISO 75-2/Bf |
| 1.8 MPa, unannealed, 3.20mm | 135 | °C | ASTM D648 |
| 1.8 MPa, unannealed, 64.0mm span 5 | 135 | °C | ISO 75-2/Af |
| Linear thermal expansion coefficient | |||
| Flow : -40 to 40°C | 5.4E-5 | cm/cm/°C | ASTM E831 |
| Flow : -40 to 40°C | 5.3E-5 | cm/cm/°C | ISO 11359-2 |
| Lateral : -40 to 40°C | 5.9E-5 | cm/cm/°C | ASTM E831 |
| Lateral : -40 to 40°C | 6.0E-5 | cm/cm/°C | ISO 11359-2 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 121 | °C | |
| Drying Time | 4.0 | hr | |
| Suggested Max Moisture | 0.020 | % | |
| Rear Temperature | 293 - 304 | °C | |
| Middle Temperature | 310 - 321 | °C | |
| Front Temperature | 321 - 332 | °C | |
| Processing (Melt) Temp | 304 - 327 | °C | |
| Mold Temperature | 82.2 - 110 | °C | |
| Back Pressure | 0.172 - 0.344 | MPa | |
| Screw Speed | 30 - 60 | rpm |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | 80*10*4 |
| 3 . | 80*10*4 |
| 4 . | 80*10*4 mm |
| 5 . | 80*10*4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| POLYlux 104 HF | Polykemi AB | PC+PBT | POLYlux |
| Xuchuan XCW-80MK(S) | Xuchuan Chemical (Suzhou) Co., Ltd | PUR, Unspecified | Xuchuan |
| OmniTech™ PET GR30 | OMNI Plastics, LLC | PET | OmniTech™ |
| Formolene® 2502A | Formosa Plastics Corporation, U.S.A. | PP Impact Copolymer | Formolene® |
| StarMed® 9015-0000 | Star Thermoplastic Alloys & Rubbers, Inc. | TPE | StarMed® |