Ronalen M40
| Category: | PP, Unspecified , Polypropylene |
| Manufacturer: | Roonamid a.s. |
| Trademark: | Ronalen |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | oP2M5t_Ronalen-M40.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Polypropylene, type reinforced with 40% micropulverized talc, natural, optimal flow properties. Suitable for injection mouldings with increased requirements to rigidity and strength. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.26 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 10 | g/10 min | ISO 1133 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 4000 | MPa | ISO 527-2 |
| Tensile Stress (Break) | 28.0 | MPa | ISO 527-2 |
| Flexural Modulus | 4200 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 2.5 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength (23°C) | 14 | kJ/m² | ISO 179/1eU |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Vicat Softening Temperature | 158 | °C | ISO 306 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | < 80.0 | °C | |
| Suggested Max Moisture | 0.10 | % | |
| Processing (Melt) Temp | 230 to 240 | °C | |
| Mold Temperature | 40.0 to 60.0 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 200 A TFE 10 | RTP Company | Nylon 6 | RTP |
| TYLON® 238HL | Tyne Plastics LLC. | Nylon 6 | TYLON® |
| Adiprene® LFG 964A | Chemtura | PUR-Ether/TDI | Adiprene® |
| Axiall PVC 9246 | Axiall Corporation | PVC, Rigid | Axiall PVC |
| Karina WHITE PVC COMPOUND 920-10/156-Y-IS-BZ | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |