Unipren® Elastomers A3 CRLA010 45A EB05IN1 UP358
| Category: | PP+EPDM , Polypropylene + EPDM Rubber |
| Manufacturer: | Petropol Industry and Trade of Polymers LTDA |
| Trademark: | Unipren® Elastomers |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | oOGqFc_Unipren-Elastomers-A3-CRLA010-45A-EB05IN1-UP358.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Thermoplastic compound based on EPDM with PP (TPE-V) dynamically vulcanized, suitable for high performance applications where outdoor exposure or resistance to high temperature (135° C) are important requirements. |
| General Information | |
|---|---|
| Features |
|
| Resin ID (ISO 1043) |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 0.900 | g/cm³ | ASTM D792 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore A) | 43 to 47 | ASTM D2240 |
| Elastomers | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress 1 | ASTM D412 | ||
| 100% Strain | 1.00 | MPa | |
| 300% Strain | 2.00 | MPa | |
| Tensile Strength 2(Break) | 7.50 | MPa | ASTM D412 |
| Tensile Elongation 3(Break) | > 750 | % | ASTM D412 |
| Compression Set | 15 | % | ASTM D395B |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Brittleness Temperature 4 | -55.0 | °C | ASTM D2137 |
| Note Message | |
|---|---|
| 1 . | Die C |
| 2 . | Die C |
| 3 . | Die C |
| 4 . | Procedure A |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 200 TFE 10 HS | RTP Company | Nylon 66 | RTP |
| tefabloc® TO 228 | Mitsubishi Chemical Performance Polymers, Inc. | SEBS | tefabloc® |
| Stanyl® TC551 | DSM Engineering Plastics | Nylon 46 | Stanyl® |
| Unipren® Elastomers A3 PRTA010 45A UP304 | Petropol Industry and Trade of Polymers LTDA | SEBS | Unipren® Elastomers |
| Alpha PE GPE 2001-R NATURAL | AlphaGary | PE, Unspecified | Alpha PE |