TARFLON™ SK3731
| Category: | PC+AS , Polycarbonate + AS |
| Manufacturer: | Idemitsu Kosan Co., Ltd. |
| Trademark: | TARFLON™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | oL6SRO_TARFLON-SK3731.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Filler reinforced, Good abrasion resist, Dimensional Precision |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| UL File Number |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.43 | g/cm³ | ISO 1183 |
| Melt Volume-Flow Rate (MVR) (260°C/2.16 kg) | 8.00 | cm³/10min | ISO 1133 |
| Spiral Flow | 21.0 | cm | Internal Method |
| Molding Shrinkage | Internal Method | ||
| Across Flow : 2.00 mm | 0.20 | % | |
| Flow : 2.00 mm | 0.17 | % |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress (Yield) | 74.0 | MPa | ISO 527-2 |
| Nominal Tensile Strain at Break | 2.0 | % | ISO 527-2 |
| Flexural Modulus | 7500 | MPa | ISO 178 |
| Flexural Stress | 106 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 4.0 | kJ/m² | ISO 179 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | 105 | °C | ISO 75-2/A |
| CLTE | ISO 11359-2 | ||
| Flow | 2.7E-5 | cm/cm/°C | |
| Transverse | 4.4E-5 | cm/cm/°C | |
| RTI Elec | 50.0 | °C | UL 746 |
| RTI Imp | 50.0 | °C | UL 746 |
| RTI Str | 50.0 | °C | UL 746 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 1.50 mm, BK | V-1 | ||
| 2.00 mm, BK | 5VB |
| Additional Information | Nominal Value | ||
|---|---|---|---|
| ISO Shortname | >PC+AS-(TD+PD)30-FR(40)< |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 to 100 | °C | |
| Drying Time | 5.0 to 8.0 | hr | |
| Rear Temperature | 270 to 280 | °C | |
| Middle Temperature | 270 to 280 | °C | |
| Front Temperature | 270 to 280 | °C | |
| Mold Temperature | 40.0 to 70.0 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| WELLAMID Nylon 6000 CP | CP-Polymer-Technik GmbH & Co. KG | Nylon 6 | WELLAMID Nylon |
| BCC Resins BC 6004 | BCC Products Inc. | Epoxy | BCC Resins |
| AKROMID® B3 GF 15 RM-M natural (3697) | AKRO-PLASTIC GmbH | Nylon 6 | AKROMID® |
| Chemraz 550 | Greene, Tweed & Co. | Perfluoroelastomer | Chemraz |
| Diakon® MH254 | Lucite International Inc. | Acrylic (PMMA) | Diakon® |