LNP™ THERMOCOMP™ 2X04505 compound
| Category: | ETFE , Ethylene Tetrafluoroethylene Copolymer |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | LNP™ THERMOCOMP™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | oKgSx5_LNPTHERMOCOMP2X04505compound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP THERMOCOMP 2X04505 is a compound based on Ethylene Tetrafluoroethylene Copolymer resin containing Carbon Fiber. Also known as: LNP* THERMOCOMP* Compound PDX-FP-E-04505 Product reorder name: 2X04505 |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | |||
| -- | 1.74 | g/cm³ | ISO 1183 |
| -- | 1.75 | g/cm³ | ASTM D792 |
| Molding Shrinkage | |||
| Flow : 24 hours | 1.0 - 1.2 | % | ASTM D955 |
| Transverse flow : 24 hours | 1.8 - 2.0 | % | ASTM D955 |
| Vertical flow direction : 24 hours | 1.9 | % | ISO 294-4 |
| Flow direction : 24 hours | 1.1 | % | ISO 294-4 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 15200 | MPa | ASTM D638 |
| -- | 11600 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Yield | 87.6 | MPa | ASTM D638 |
| Yield | 89.0 | MPa | ISO 527-2 |
| Fracture | 85.5 | MPa | ASTM D638 |
| Fracture | 88.0 | MPa | ISO 527-2 |
| Tensile Elongation | |||
| Yield | 4.5 | % | ASTM D638 |
| Yield | 4.7 | % | ISO 527-2 |
| Fracture | 4.8 | % | ASTM D638 |
| Fracture | 4.9 | % | ISO 527-2 |
| Flexural Modulus | |||
| -- | 10300 | MPa | ASTM D790 |
| -- | 18800 | MPa | ISO 178 |
| Flexural Stress | 319 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | |||
| 23°C | 270 | J/m | ASTM D256 |
| 23°C 2 | 24 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact | |||
| 23°C | 1000 | J/m | ASTM D4812 |
| 23°C 3 | 59 | kJ/m² | ISO 180/1U |
| Instrumented Dart Impact | |||
| 23°C, Energy at Peak Load | 18.8 | J | ASTM D3763 |
| -- | 8.90 | J | ISO 6603-2 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, unannealed, 3.20mm | 255 | °C | ASTM D648 |
| 0.45 MPa, unannealed, 64.0mm span 4 | 251 | °C | ISO 75-2/Bf |
| 1.8 MPa, unannealed, 3.20mm | 222 | °C | ASTM D648 |
| 1.8 MPa, unannealed, 64.0mm span 5 | 207 | °C | ISO 75-2/Af |
| Linear thermal expansion coefficient | |||
| Flow : -40 to 40°C | 7.7E-5 | cm/cm/°C | ASTM E831 |
| Flow : -40 to 40°C | 7.8E-5 | cm/cm/°C | ISO 11359-2 |
| Lateral : -40 to 40°C | 1.3E-5 | cm/cm/°C | ASTM E831 |
| Lateral : -40 to 40°C | 1.2E-5 | cm/cm/°C | ISO 11359-2 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 121 - 149 | °C | |
| Drying Time | 4.0 | hr | |
| Rear Temperature | 282 - 293 | °C | |
| Middle Temperature | 310 - 321 | °C | |
| Front Temperature | 332 - 343 | °C | |
| Processing (Melt) Temp | 316 | °C | |
| Mold Temperature | 93.3 - 121 | °C | |
| Back Pressure | 0.172 - 0.344 | MPa | |
| Screw Speed | 30 - 60 | rpm |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | 80*10*4 |
| 3 . | 80*10*4 |
| 4 . | 80*10*4 mm |
| 5 . | 80*10*4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SIMONA® SIMOPOR-COLOR | SIMONA AMERICA, Inc. | PVC, Unspecified | SIMONA® |
| Zhongfa PP ZF-ZR2 | Yuyao Zhongfa Engineering Plastics Co. Ltd. | PP, Unspecified | Zhongfa |
| InnoClear™ VA-273 | Innovative Polymers, Inc. | TSU | InnoClear™ |
| Plenco 01506 (Injection) | Plastics Engineering Co. | Polyester, TS | Plenco |
| Sylvin 8215-82 Purple 8424 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |