LNP™ THERMOCOMP™ YF004 compound
| Category: | TPEE , Thermoplastic Polyester Elastomer |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | LNP™ THERMOCOMP™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | oIRG3F_LNP-THERMOCOMP-YF004-compound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP THERMOCOMP* YF004 is a compound based on Polyester Elastomer resin containing Glass Fiber. Also known as: LNP* Thermocomp* Compound YF-1004 Product Reorder name: YF004 |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.35 | g/cm³ | ASTM D792 |
| Molding Shrinkage | ASTM D955 | ||
| Flow : 24 hr | 0.20 to 0.40 | % | |
| Across Flow : 24 hr | 0.60 to 0.80 | % | |
| Water Absorption | |||
| 24 hr, 50% RH | 0.71 | % | ASTM D570 |
| Equilibrium, 23°C, 50% RH | 0.71 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 2640 | MPa | ASTM D638 |
| -- | 2170 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Break 2 | 47.8 | MPa | ASTM D638 |
| Break | 48.0 | MPa | ISO 527-2/5 |
| Tensile Elongation | |||
| Break 3 | 12 | % | ASTM D638 |
| Break | 13 | % | ISO 527-2/5 |
| Flexural Modulus | |||
| 50.0 mm Span 4 | 1930 | MPa | ASTM D790 |
| -- 5 | 312 | MPa | ISO 178 |
| Flexural Stress | |||
| -- | 25.7 | MPa | ISO 178 |
| Break, 50.0 mm Span 6 | 55.4 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | |||
| 23°C | 400 | J/m | ASTM D256 |
| 23°C 7 | 37 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact (23°C) | No Break | ASTM D4812, ISO 180/1U | |
| Instrumented Dart Impact | |||
| 23°C, Total Energy | 14.5 | J | ASTM D3763 |
| -- | 10.1 | J | ISO 6603-2 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, Unannealed, 3.20 mm | 186 | °C | ASTM D648 |
| 0.45 MPa, Unannealed, 64.0 mm Span 8 | 184 | °C | ISO 75-2/Bf |
| 1.8 MPa, Unannealed, 3.20 mm | 151 | °C | ASTM D648 |
| 1.8 MPa, Unannealed, 64.0 mm Span 9 | 129 | °C | ISO 75-2/Af |
| CLTE | ASTM D696 | ||
| Flow : -30 to 30°C | 1.2E-4 | cm/cm/°C | |
| Transverse : -30 to 30°C | 3.2E-5 | cm/cm/°C |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 82.2 | °C | |
| Drying Time | 4.0 | hr | |
| Suggested Max Moisture | 0.10 | % | |
| Rear Temperature | 182 to 193 | °C | |
| Middle Temperature | 204 to 216 | °C | |
| Front Temperature | 227 to 238 | °C | |
| Processing (Melt) Temp | 216 to 238 | °C | |
| Mold Temperature | 26.7 to 54.4 | °C | |
| Back Pressure | 0.172 to 0.344 | MPa | |
| Screw Speed | 30 to 60 | rpm |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | Type I, 5.0 mm/min |
| 3 . | Type I, 5.0 mm/min |
| 4 . | 1.3 mm/min |
| 5 . | 2.0 mm/min |
| 6 . | 1.3 mm/min |
| 7 . | 80*10*4 |
| 8 . | 80*10*4 mm |
| 9 . | 80*10*4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Rynite® RE15022 NC010 | DuPont Performance Polymers | PET | Rynite® |
| Bakelite® PF 51 | Hexion Inc. | Phenolic | Bakelite® |
| Karina IVORY PVC COMPOUND 851-35/ 1-E-IS-LMP | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| Sylvin 3200-60 Clear | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| Sylvin 9789-73 Black | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |