INNOMID® CS 6-9830
| Category: | Nylon 6 Alloy , Polyamide 6 Alloy |
| Manufacturer: | Inno-Comp Ltd. |
| Trademark: | INNOMID® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | oH0CQv_INNOMID-CS-6-9830.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
INNOMID ® CS 6-9830 is a 30 % glass-fibre-filled polyamide (PA-6) compound. This grade is available in nature and custom coloured form. Recommended application INNOMID ® CS 6-9830 is recommended for producing injection moulded products, where the required properties are high strength and stiffness. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Resin ID (ISO 1043) |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density (23°C) | 1.36 | g/cm³ | ISO 1183 |
| Melt Volume-Flow Rate (MVR) (275°C/5.0 kg) | 46.0 | cm³/10min | ISO 1133 |
| Molding Shrinkage | ISO 294-4 | ||
| Vertical flow direction | 0.70 | % | ISO 294-4 |
| Flow direction | 0.10 | % | ISO 294-4 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 9400 | MPa | ISO 527-2/2 |
| Tensile Stress (Break) | 150 | MPa | ISO 527-2/1A/50 |
| Flexural Modulus 1 | 6600 | MPa | ISO 178 |
| Flexural Stress 2 | 245 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | ||
| -30°C | 9.0 | kJ/m² | ISO 179/1eA |
| 23°C | 11 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength | ISO 179/1eU | ||
| -30°C | 69 | kJ/m² | ISO 179/1eU |
| 23°C | 73 | kJ/m² | ISO 179/1eU |
| Notched Izod Impact | ISO 180/A | ||
| -30°C | 9.0 | kJ/m² | ISO 180/A |
| 23°C | 11 | kJ/m² | ISO 180/A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, not annealed | 220 | °C | ISO 75-2/B |
| 1.8 MPa, not annealed | 200 | °C | ISO 75-2/A |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | 1.0E+15 | ohms·cm | DIN 53482 |
| Comparative Tracking Index (Solution A) | 550 | V | IEC 60112 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (3.20 mm) | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 60.0 - 80.0 | °C | |
| Suggested Max Moisture | 0.10 | % | |
| Rear Temperature | 220 - 260 | °C | |
| Middle Temperature | 220 - 260 | °C | |
| Front Temperature | 220 - 260 | °C | |
| Processing (Melt) Temp | 240 - 260 | °C | |
| Mold Temperature | 60.0 - 100 | °C | |
| Injection Rate | Moderate |
| Injection instructions |
|---|
| Holding Pressure: 50-100% of actual injection pressure |
| Note Message | |
|---|---|
| 1 . | Type 1A, 2.0 mm/min |
| 2 . | Type 1A, 2.0 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Rilsamid® AMNO P40 TLD | Arkema | Nylon 12 | Rilsamid® |
| Sindustris PBT TE5001GU | Sincerity Australia Pty Ltd. | PC+PBT | Sindustris PBT |
| Altuglas® SG7 | Altuglas International of Arkema Inc. | Acrylic (PMMA) | Altuglas® |
| Axiall PVC 6704 | Axiall Corporation | PVC, Flexible | Axiall PVC |
| Lucent PBT LPB-130 | Lucent Polymers, Inc. | PBT | Lucent PBT |