LNP™ THERMOCOMP™ AR002XXH compound
| Category: | ABS , Acrylonitrile Butadiene Styrene |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | LNP™ THERMOCOMP™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | oGs40C_LNP-THERMOCOMP-AR002XXH-compound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP THERMOCOMP AR002XXH is a compound based on ABS resin containing 10% Barium Sulfate. Also known as: LNP* THERMOCOMP* Compound AR002XXH Product reorder name: AR002XXH |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.12 | g/cm³ | ASTM D792 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus 1 | 2400 | MPa | ASTM D638 |
| Tensile Strength 2(Break) | 40.0 | MPa | ASTM D638 |
| Tensile Elongation 3(Break) | 2.6 | % | ASTM D638 |
| Flexural Modulus 4(50.0 mm Span) | 2560 | MPa | ASTM D790 |
| Flexural Strength 5(Break, 50.0 mm Span) | 68.0 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 84 | J/m | ASTM D256 |
| Unnotched Izod Impact (23°C) | 270 | J/m | ASTM D4812 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed, 3.20 mm) | 78.0 | °C | ASTM D648 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 82.2 | °C | |
| Drying Time | 4.0 | hr | |
| Suggested Max Moisture | 0.050 to 0.10 | % | |
| Rear Temperature | 204 to 216 | °C | |
| Middle Temperature | 232 to 243 | °C | |
| Front Temperature | 266 to 277 | °C | |
| Processing (Melt) Temp | 260 | °C | |
| Mold Temperature | 71.1 to 82.2 | °C | |
| Back Pressure | 0.172 to 0.344 | MPa | |
| Screw Speed | 30 to 60 | rpm |
| Note Message | |
|---|---|
| 1 . | 5.0 mm/min |
| 2 . | Type I, 5.0 mm/min |
| 3 . | Type I, 5.0 mm/min |
| 4 . | 1.3 mm/min |
| 5 . | 1.3 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Cheng Yu SW10 | Cheng Yu Plastic Company Limited | Acetal (POM) Copolymer | Cheng Yu |
| Geon™ Vinyl Flexible A90U2 | PolyOne Corporation | PVC, Flexible | Geon™ Vinyl Flexible |
| LEXAN™ EXL9414T resin | SABIC Innovative Plastics Asia Pacific | PC | LEXAN™ |
| Karina IVORY PVC COMPOUND 760-35/1-IS-SD | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| EPAMOULD 295A83W | Epaflex Polyurethanes S.R.L. | TPU-Polyester | EPAMOULD |