POLYfill PP CQX30030 RTX
| Category: | PP, Unspecified , Polypropylene |
| Manufacturer: | Polykemi AB |
| Trademark: | POLYfill |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | oGIX3x_POLYfill-PP-CQX30030-RTX.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Mineral reinforced Scratch resistant |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.13 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 30 | g/10 min | ISO 1133 |
| Molding Shrinkage | ISO 294-4 | ||
| Across Flow | 1.2 to 1.4 | % | |
| Flow | 1.2 to 1.4 | % |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress | 19.0 | MPa | ISO 527-2 |
| Tensile Strain | ISO 527-2 | ||
| Yield | 8.0 | % | |
| Break | 36 | % | |
| Flexural Modulus (23°C) | 1900 | MPa | ISO 178 |
| Flexural Stress | 37.0 | MPa | ISO 178 |
| Scratch Resistance - 10 N Fine Structure 1 | < 0.100 | dL | ISO 1518/D65 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179 | ||
| -20°C | 3.0 | kJ/m² | |
| 23°C | 4.0 | kJ/m² | |
| Charpy Unnotched Impact Strength | ISO 179 | ||
| -20°C | 21 | kJ/m² | |
| 23°C | 36 | kJ/m² |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature 2 | |||
| 0.45 MPa, Unannealed | 110 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 58.0 | °C | ISO 75-2/A |
| Vicat Softening Temperature | |||
| -- | 148 | °C | ISO 306/A50 |
| -- | 75.0 | °C | ISO 306/B50 |
| CLTE - Flow | 7.0E-5 to 9.0E-5 | cm/cm/°C | Internal Method |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (1.60 mm) | HB | UL 94 | |
| Glow Wire Ignition Temperature (2.00 mm) | 750 | °C | IEC 60695-2-13 |
| Note Message | |
|---|---|
| 1 . | Test performed on black plaques with fine (Standex MT9078) and rough (Standex MT11435) structure |
| 2 . | 120°C/hr |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Santoprene™ 123-50W175 | ExxonMobil Chemical | TPV | Santoprene™ |
| Supol HT320E | LyondellBasell Industries | PP Copolymer | Supol |
| Arak LLDPE HD5050UA | Shazand (Arak) Petrochemical Corporation | HDPE | Arak LLDPE |
| Sinvicomp SSZ6309 KD11 | Teknor Apex Asia Pacific PTE. LTD. | PVC, Flexible | SINVICOMP |
| Axiall PVC 1501 | Axiall Corporation | PVC, Flexible | Axiall PVC |