Taitalac® 1002
| Category: | ABS , Acrylonitrile Butadiene Styrene |
| Manufacturer: | Taita Chemical Company, Ltd. |
| Trademark: | Taitalac® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | oGI4XY_Taitalac-1002.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Taitalac ABS 1002 is a high flow resin that features outstanding processability and high productivity. Uses include large or complex shaped products, TV housings, vacuum cleaners, various leisure goods, air conditioners, cash registers and floppy disks. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.03 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (200°C/5.0 kg) | 2.3 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow | 0.40 | % | ASTM D955 |
| Water Absorption (24 hr) | 0.30 | % | ASTM D570 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 112 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | ASTM D638 | ||
| Yield, 23°C, 3.18mm | 40.7 | MPa | ASTM D638 |
| Fracture, 23°C, 3.18mm | 35.2 | MPa | ASTM D638 |
| Tensile Elongation (Break, 23°C) | 30 | % | ASTM D638 |
| Flexural Modulus 1(23°C) | 2550 | MPa | ASTM D790 |
| Flexural Strength 2(Yield, 23°C) | 71.0 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C, 12.7 mm) | 230 | J/m | ASTM D256A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 82.8 | °C | ASTM D648 |
| Vicat Softening Temperature | 97.8 | °C | ASTM D1525 |
| RTI Elec (1.57 mm) | 60.0 | °C | UL 746 |
| RTI Imp (1.57 mm) | 60.0 | °C | UL 746 |
| RTI (1.57 mm) | 60.0 | °C | UL 746 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| High Amp Arc Ignition (HAI) (1.57 mm) | 200 | UL 746 | |
| High Voltage Arc Tracking Rate (HVTR) (1.57 mm) | 0.00254 | mm/min | UL 746 |
| Hot-wire Ignition (HWI) (1.57 mm) | 16 | sec | UL 746 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (1.59 mm) | HB | UL 94 |
| Additional Information |
|---|
| Melt Flow Rate, ASTM D1238, 200°C, 5kg: 1.5 to 3.0 g/10min |
| Note Message | |
|---|---|
| 1 . | 2.8 mm/min |
| 2 . | 2.8 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Asrene® SF 5007 | Chandra Asri Petrochemical | HDPE | Asrene® |
| FERREX® GPP20CF15HB | Ferro Corporation | PP Homopolymer | FERREX® |
| 3M™ Dyneon™ Fluoroelastomer FC 2230 | 3M Advanced Materials Division | Fluorelastomer | 3M™ Dyneon™ Fluoroelastomer |
| HiFill® PP GF/M35 CC BK | Techmer Engineered Solutions | PP, Unspecified | HiFill® |
| Novalloy-B B5726 | PlastxWorld Inc. | ABS+PBT | Novalloy-B |