Petrothene® NA980000
| Category: | LDPE , Low Density Polyethylene |
| Manufacturer: | LyondellBasell Industries |
| Trademark: | Petrothene® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | oFKgDg_Petrothene-NA980000.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Petrothene NA980 is a low density homopolymer resin selected by customers for use in shrink packaging, bundling, pallet wrap and heavy-duty liner applications. Excellent bubble stability, melt strength, impact and shrinkage are key attributes of NA980. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.920 | g/cm³ | ASTM D1505 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 0.25 | g/10 min | ASTM D1238 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore D) | 45 | ASTM D2240 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | ASTM D638 | ||
| Yield | 9.79 | MPa | ASTM D638 |
| Fracture | 17.9 | MPa | ASTM D638 |
| Tensile Elongation | ASTM D638 | ||
| Yield | 100 | % | ASTM D638 |
| Fracture | 700 | % | ASTM D638 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film Thickness - Tested | 51 | µm | |
| secant modulus | ASTM D882 | ||
| 1% secant, MD : 51 µm | 207 | MPa | ASTM D882 |
| 1% secant, TD : 51 µm | 241 | MPa | ASTM D882 |
| Tensile Strength | ASTM D882 | ||
| MD : Yield, 51 µm | 20.7 | MPa | ASTM D882 |
| TD : Yield, 51 µm | 19.0 | MPa | ASTM D882 |
| Tensile Elongation | ASTM D882 | ||
| MD : Fracture, 51 µm | 310 | % | ASTM D882 |
| TD : Fracture, 51 µm | 430 | % | ASTM D882 |
| Dart Drop Impact (51 µm) | 180 | g | ASTM D1709 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Brittleness Temperature | -75.0 | °C | ASTM D746 |
| Vicat Softening Temperature | 93.0 | °C | ASTM D1525 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Melt Temperature | 166 - 221 | °C |
| Extrusion instructions |
|---|
| Optimum properties are obtained at melt temperatures between 330°-430°F (165°-221°C) and a blow-up ratio between 1.7-3.0:1, using proper techniques and equipment. |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Pro-fax SLY332 | INDELPRO, S.A. de C.V. | PP Homopolymer | Pro-fax |
| Trexprene® A74CI | Mitsubishi Chemical Performance Polymers, Inc. | TPV | Trexprene® |
| Nipol® NBR DN003 | Zeon Corporation | NBR | Nipol® NBR |
| LNP™ THERMOCOMP™ DX11354X compound | SABIC Innovative Plastics Asia Pacific | PC | LNP™ THERMOCOMP™ |
| TechnoElast V A7000 I 2 sw | TechnoCompound GmbH | TPE | TechnoElast |