mPact™ D139
| Category: | mLLDPE , Metallocene Linear Low Density Polyethylene |
| Manufacturer: | Chevron Phillips Chemical Company LLC |
| Trademark: | mPact™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | oESvnH_mPact-D139.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
This mLLDPE is tailored for applications that require:
Typical blown film applications include:
|
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.918 | g/cm³ | ASTM D1505 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 1.0 | g/10 min | ASTM D1238 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Coefficient of Friction (Blown Film) | > 1.0 | ASTM D1894 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film Thickness - Tested | 25 | µm | |
| secant modulus | ASTM D882 | ||
| 1% secant, MD : 25 µm, blown film | 179 | MPa | ASTM D882 |
| 1% secant, TD : 25 µm, blown film | 208 | MPa | ASTM D882 |
| Tensile Strength | ASTM D882 | ||
| MD : Yield, 25 µm, blown film | 12.8 | MPa | ASTM D882 |
| TD : Yield, 25 µm, blown film | 10.0 | MPa | ASTM D882 |
| MD : Broken, 25 µm, blown film | 74.5 | MPa | ASTM D882 |
| TD : Broken, 25 µm, blown film | 57.0 | MPa | ASTM D882 |
| Tensile Elongation | ASTM D882 | ||
| MD : Broken, 25 µm, blown film | 500 | % | ASTM D882 |
| TD : Broken, 25 µm, blown film | 600 | % | ASTM D882 |
| Dart Drop Impact (25 µm, Blown Film) | > 700 | g | ASTM D1709 |
| Elmendorf Tear Strength | ASTM D1922 | ||
| MD : 25 µm, blown film | 220 | g | ASTM D1922 |
| TD : 25 µm, blown film | 430 | g | ASTM D1922 |
| Seal Initiation Temperature 1(25 µm, Blown Film) | 102 | °C | ASTM F88 |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Gloss (60°, 25.4 µm, Blown Film) | 130 | ASTM D2457 | |
| Haze (25.4 µm, Blown Film) | 4.0 | % | ASTM D1003 |
| Additional Information |
|---|
| Blown Film produced on LLDPE line, 2.5:1 BUR, 80 mil Die Gap 8 in Die, 250 lbs/hr, 400°F Melt Temperature. |
| Note Message | |
|---|---|
| 1 . | Temperature at which 0.3 lb/in heat seal strength is achieved. 0.5 s dwell, 30 psi pressure, 11.8 in/min separation rate. |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Geon™ Vinyl Rigid Molding M5105 | PolyOne Corporation | PVC, Rigid | Geon™ Vinyl Rigid Molding |
| ICORENE® 2910 | ICO Polymers EMEA, A Division of A. Schulman | Plastomer | ICORENE® |
| INLUBE POMCGF10TF15 | Infinity LTL Engineered Compounds | Acetal (POM) Copolymer | INLUBE |
| Jamplast JPLGABSI | Jamplast, Inc. | ABS | Jamplast |
| Karina BLACK PVC COMPOUND 807D48/1-C-IS | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |