POLYFLAM® SDR 5005
| Category: | PS (GPPS) , General Purpose Polystyrene |
| Manufacturer: | A. Schulman Europe |
| Trademark: | POLYFLAM® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | oDiq7h_POLYFLAM-SDR-5005.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Flame retardant PS standard grade, without PBDE and HBCD |
| General Information | |
|---|---|
| Features |
|
| UL File Number |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.06 | g/cm³ | ISO 1183/A |
| Melt Volume-Flow Rate (MVR) (200°C/5.0 kg) | 12.5 | cm³/10min | ISO 1133 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 2550 | MPa | ISO 527-2/1A/1 |
| Tensile Stress | |||
| Yield | 33.0 | MPa | ISO 527-2/1A/50 |
| Fracture | 27.0 | MPa | ISO 527-2/50 |
| Tensile Strain (Yield) | 1.6 | % | ISO 527-2/1A/50 |
| Nominal Tensile Strain at Break | 35 | % | ISO 527-2/50 |
| Flexural Modulus 1 | 2700 | MPa | ISO 178 |
| Flexural Stress 2 | ISO 178 | ||
| 3.5% strain | 49.0 | MPa | ISO 178 |
| 5.3% strain | 50.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | ||
| -30°C | 5.0 | kJ/m² | ISO 179/1eA |
| 23°C | 7.0 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength | ISO 179/1eU | ||
| -30°C | 60 | kJ/m² | ISO 179/1eU |
| 23°C | 70 | kJ/m² | ISO 179/1eU |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, not annealed | 79.0 | °C | ISO 75-2/Bf |
| 1.8 MPa, not annealed | 73.0 | °C | ISO 75-2/Af |
| Vicat Softening Temperature | |||
| -- | 92.0 | °C | ISO 306/A50 |
| -- | 85.0 | °C | ISO 306/B50 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | UL 94, IEC 60695-11-10, -20 | ||
| 1.50 mm | V-2 | UL 94, IEC 60695-11-10, -20 | |
| 3.00 mm | V-2 | UL 94, IEC 60695-11-10, -20 | |
| Glow Wire Flammability Index | IEC 60695-2-12 | ||
| 1.50 mm | 960 | °C | IEC 60695-2-12 |
| 3.00 mm | 960 | °C | IEC 60695-2-12 |
| Glow Wire Ignition Temperature | IEC 60695-2-13 | ||
| 1.50 mm | 825 | °C | IEC 60695-2-13 |
| 3.00 mm | 825 | °C | IEC 60695-2-13 |
| Additional Information |
|---|
| 1.) Not for use in food contact applications2.) Not for use in medical or pharmaceutical applications |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 70.0 - 80.0 | °C | |
| Drying Time | 2.0 - 4.0 | hr | |
| Rear Temperature | 170 | °C | |
| Middle Temperature | 190 | °C | |
| Front Temperature | 190 | °C | |
| Nozzle Temperature | 200 | °C | |
| Processing (Melt) Temp | 170 - 200 | °C | |
| Mold Temperature | 30.0 - 60.0 | °C | |
| Injection Pressure | 80.0 - 120 | MPa | |
| Injection Rate | Slow-Moderate | ||
| Holding Pressure | 40.0 - 90.0 | MPa | |
| Back Pressure | 5.00 - 10.0 | MPa | |
| Cushion | < 5.00 | mm | |
| Screw Speed | mm/sec |
| Note Message | |
|---|---|
| 1 . | 2.0 mm/min |
| 2 . | 2.0 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| TAROMID A 280 MT6 | Taro Plast S.p.A. | Nylon 66 | TAROMID A |
| NEXUS Reprocessed Nylon 6 G16 RBK | Nexus Resin Group, LLC. | Nylon 6 | NEXUS Reprocessed |
| Alkatuff® LL711UV | Qenos Pty Ltd | LLDPE | Alkatuff® |
| Lupoy® 1080-70 | LG Chem Ltd. | PC | Lupoy® |
| Rotuba CA MH | Rotuba Extruders, Inc. | CA | Rotuba CA |